Hostaform® C 13021 RM

ジェネリックファミリー：聚甲醛（POM）共聚物 • 提供元： Celanese Corporation

Injection molding grade with moderate flow; with improved friction properties
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 29988- POM-K, M-GNS, 04-002 POM copolymer Easy flowing Injection molding type, similar to C 13021 but modified for sliding combinations HOSTAFORM/HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: favourite applications with sliding combinations HOSTAFORM/HOSTAFORM, e.g. for smooth-running zippers, also sliding combinations with other plastics are possible. FMVSS = Federal Motor Vehicle Safety Standard (USA)

一般的な属性

Prospectorで無料のアカウントを作成し、Hostaform® C 13021 RMのデータシート詳細すべてにアクセスします。そこで、物理、機械、硬度仕様に関するすべての情報をご覧ください

材料ステータス

已商用：当前有效

ドキュメント

Technical Datasheet

ドキュメントのダウンロード

可用性

欧洲, 非洲和中东, 北美洲, 拉丁美洲, 亚太地区

用途

汽车领域的应用

自動車の仕様

CONTINENTAL TST N 055 54.32

加工方法

注射成型

マルチポイントデータ

Isothermal Stress vs. Strain (ISO 11403)
Secant Modulus vs. Strain (ISO 11403)
Shear Stress vs. Shear Rate (ISO 11403)
Viscosity vs. Shear Rate (ISO 11403)

その他の属性

添加剂, 特性, 形式, 密度, 熔融体积流量（MVR）, 收缩率, 吸水率Sat/23C, 吸水率23C/50RH, 拉伸模量, 拉伸屈服应力, 拉伸屈服应变, 标称拉伸断裂应变, 拉伸蠕变模量 (1h), 拉伸蠕变模量 (1000h), 弯曲模量, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, 球压硬度, DTUL (1.80 MPa) 未退火, 维卡软化温度, 熔融温度, 线性热膨胀系数，流动, 表面电阻率, 体积电阻率, 介电强度, 相对电容率, 耗散因数, 相比耐漏电起痕指数(CTI), 其他性能, 干燥温度, 干燥时间, 建议的最大水分含量, 料斗温度, 料筒后部温度, 料筒中部温度, 料筒前部温度, 射嘴温度, 加工（熔体）温度, 模具温度, 注射速度, 背压

プラスチックでは、41個の属性にアクセスします。無料アカウントを作成されるか、Prospectorにサインインしてください。