Fluoropolymer: Cri-Line
| 製品 | 可用性 | 製品の説明 |
|---|---|---|
| Cri-Line IF-915 | 北アメリカ |
68% Fluorine terpolymers formulated for improved chemical resistance. IF compounds are good choices for fuel applications.
|
| Cri-Line LC-508-55 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-512-55-BR | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-608 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-612 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-612-LV | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-LV compounds are also injection moldable.
|
| Cri-Line LC-612-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LC-615-65 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-615-65-LV | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-LV compounds are also injection moldable.
|
| Cri-Line LC-615-65-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LC-712-BR | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-715 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-715-75 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-715-75-LV | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-LV compounds are also injection moldable.
|
| Cri-Line LC-715-75-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LC-715-LV | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-LV compounds are also injection moldable.
|
| Cri-Line LC-715-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LC-815 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-815-85 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-815-85-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LC-815-LV | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-LV compounds are also injection moldable.
|
| Cri-Line LC-815-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LC-915 | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-915-BR | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC compounds are used in lathe cut and custom molded goods, including value stem seals.
|
| Cri-Line LC-915-LV | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-LV compounds are also injection moldable.
|
| Cri-Line LC-915-THK | 北アメリカ |
66% Fluorine copolymers formulated for low cost. LC-THK compounds are fissure resistant in thick cross sections; these compounds also exhibit enhanced rubber-to-metal bonding.
|
| Cri-Line LS-715 | 北アメリカ |
The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles.
|
| Cri-Line LS-918 | 北アメリカ |
The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles.
|
| Cri-Line LT-718 | 北アメリカ |
High fluorine tetrapolymers formulated for low temperature flexibility. HFLT compounds are excellent choices for fuel applications, including methanol-containing fuels, where low temperature flexibility is also essential. The LT compounds are designed for low temperature applications.
|
| Cri-Line LT-718-75 | 北アメリカ |
High fluorine tetrapolymers formulated for low temperature flexibility. HFLT compounds are excellent choices for fuel applications, including methanol-containing fuels, where low temperature flexibility is also essential. The LT compounds are designed for low temperature applications.
|
| Cri-Line NPC-720 | 北アメリカ |
The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles.
|
| Cri-Line NPC-820 | 北アメリカ |
The LS compounds are designed to give part shrinkage (out of the mold) and post-curing operation comparable to a nitrile or similar elastomer. In most cases, tooling changes are not required when switching over to an LS compound. NPC indicates no post cure required to achieve high tensile and modulus values with good compression set and aging characteristics. FKHT is a high temperature resistant, low compression set compound. FKX is a high viscosity, high green strength, black fluorocarbon compound formulated for HAV and / or salt bath curing of O-ring cord and extruded profiles.
|
| Cri-Line SP-508 | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-510-55 | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-612 | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-615-65 | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-715 | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-715-75 | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-715-75-LV | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|
| Cri-Line SP-715-THK | 北アメリカ |
66% Fluorine copolymers formulated for the ultimate in compression resistance. SP compounds are the best choice for O-rings.
|