Home > Plastics > Materials > 4LOY® > 4LOY® 10E27200 FR1 - Datasheet

4LOY® 10E27200 FR1 Datasheet

Polycarbonate + ABS

Supplied by 4Plas

View Complete Data Sheet Search 118000+ Data Sheets
Create Your Free Account! or Login
Product Description
4LOY 10E27200 FR1 is a Standard Flow 65% PC / 35% ABS FR-V0 PC/ABS
General  
Material Status 
  • Commercial: Active
Availability 
  • Europe
Processing Method 
  • Injection Molding
Physical
Nominal Value
Unit
Test Method
Density
g/cm³
ISO 1183
Molding Shrinkage - Flow
%
 
Water Absorption 2 (Equilibrium, 73°F, 50% RH)
%
ISO 62
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus (73°F)
psi
ISO 527-2/5
Tensile Stress (Break, 73°F)
psi
ISO 527-2/5
Tensile Strain (Break, 73°F)
%
ISO 527-2/5
Impact
Nominal Value
Unit
Test Method
Notched Izod Impact Strength (73°F)
ft·lb/in²
ISO 180/1A
Thermal
Nominal Value
Unit
Test Method
Heat Deflection Temperature
     
66 psi, Unannealed
°F
ISO 75-2/B
264 psi, Unannealed
°F
ISO 75-2/A
Vicat Softening Temperature
°F
ISO 306/B
Flammability
Nominal Value
Unit
Test Method
Flame Rating
    UL 94
0,06 in
 
 
0,13 in
 
 
Glow Wire Flammability Index (0,08 in)
°F
IEC 60695-2-12
Available Documents
Processing (English)
Technical Datasheet (English)
Injection
Nominal Value
Unit
 
Drying Temperature
°F
 
Drying Time
hr
 
Suggested Max Moisture
%
 
Processing (Melt) Temp
°F
 
Mold Temperature
°F
 
Injection Rate
 
 
Holding Pressure
psi
 
Screw Speed
rpm
 
Injection Notes
Feed Throat Temperature: 60 - 80 °C
Back Pressure: Low
Notes
1Typical properties: these are not to be construed as specifications.
224 Hrs
 
UL and the UL logo are trademarks of UL LLC © 2016. All Rights Reserved.
The information presented on this datasheet was acquired by UL Prospector from the producer of the material. UL Prospector makes substantial efforts to assure the accuracy of this data. However, UL Prospector assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.