| Product Description | ||||
|
30% glass reinforced, UL94 V-0/5V rated. Numerous applications: edge trimmers, food mixer motor stator and commutator, cooling fan, connectors, bobbins, switches etc
|
||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
Filler / Reinforcement
|
|
|||
|
Uses
|
|
|||
|
Automotive Specifications
|
|
|||
|
Processing Method
|
|
|||
|
Multi-Point Data
|
|
|||
|
Also Available In
|
|
|||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
|||
|
--
|
|
|
ASTM D792 |
|
--
|
|
g/cm³
|
ISO 1183 |
|
Specific Volume
|
|
in³/lb
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg)
|
|
g/10 min
|
ASTM D1238 |
|
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)
|
|
in³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
Internal Method | ||
|
Flow
2
|
|
in/in
|
|
|
Flow
: 0.126 in
|
|
in/in
|
|
|
Across Flow
2
|
|
in/in
|
|
|
Across Flow
: 0.126 in
|
|
in/in
|
|
|
Water Absorption
|
ISO 62 | ||
|
Saturation, 73°F
|
|
%
|
|
|
Equilibrium, 73°F, 50% RH
|
|
%
|
|
|
Outdoor Suitability
|
|
|
UL 746C |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
|||
|
-- 3
|
|
psi
|
ASTM D638 |
|
--
|
|
psi
|
ISO 527-2/1 |
|
Tensile Strength
|
|||
|
Yield 4
|
|
psi
|
ASTM D638 |
|
Yield
|
|
psi
|
ISO 527-2/5 |
|
Break 4
|
|
psi
|
ASTM D638 |
|
Break
|
|
psi
|
ISO 527-2/5 |
|
Tensile Elongation
|
|||
|
Yield 4
|
|
%
|
ASTM D638 |
|
Yield
|
|
%
|
ISO 527-2/5 |
|
Break 4
|
|
%
|
ASTM D638 |
|
Break
|
|
%
|
ISO 527-2/5 |
|
Flexural Modulus
|
|||
|
1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
-- 6
|
|
psi
|
ISO 178 |
|
Flexural Stress
|
|||
|
--
|
|
psi
|
ISO 178 |
|
Break, 1.97 in Span 5
|
|
psi
|
ASTM D790 |
|
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel)
|
|
mg
|
Internal Method |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength 7
|
ISO 179/1eA | ||
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Charpy Unnotched Impact Strength 7
|
ISO 179/1eU | ||
|
-22°F
|
|
ft·lb/in²
|
|
|
73°F
|
|
ft·lb/in²
|
|
|
Notched Izod Impact
|
|||
|
-22°F
|
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
|
ft·lb/in
|
ASTM D256 |
|
-22°F 8
|
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 8
|
|
ft·lb/in²
|
ISO 180/1A |
|
Unnotched Izod Impact
|
|||
|
73°F
|
|
ft·lb/in
|
ASTM D4812 |
|
-22°F 8
|
|
ft·lb/in²
|
ISO 180/1U |
|
73°F 8
|
|
ft·lb/in²
|
ISO 180/1U |
|
Instrumented Dart Impact (73°F, Total Energy)
|
|
in·lb
|
ASTM D3763 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
|
|
ASTM D785, ISO 2039-2 |
|
Ball Indentation Hardness (H 358/30)
|
|
psi
|
ISO 2039-1 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
66 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
66 psi, Unannealed, 0.157 in, 3.94 in Span 9
|
|
°F
|
ISO 75-2/Be |
|
264 psi, Unannealed, 0.126 in
|
|
°F
|
ASTM D648 |
|
264 psi, Unannealed, 0.157 in, 3.94 in Span 9
|
|
°F
|
ISO 75-2/Ae |
|
264 psi, Unannealed, 0.157 in, 2.52 in Span 8
|
|
°F
|
ISO 75-2/Af |
|
Vicat Softening Temperature
|
|||
|
--
|
|
°F
|
ASTM D1525 10, ISO 306/B50, ISO 306/B120 |
|
--
|
|
°F
|
ISO 306/A50 |
|
Ball Pressure Test (253 to 261°F)
|
|
|
IEC 60695-10-2 |
|
CLTE
|
|||
|
Flow
: -40 to 104°F
|
|
in/in/°F
|
ASTM E831, ISO 11359-2 |
|
Flow
: 73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse
: -40 to 104°F
|
|
in/in/°F
|
ASTM E831 |
|
Transverse
: -40°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Transverse
: 73 to 176°F
|
|
in/in/°F
|
ISO 11359-2 |
|
Thermal Conductivity
|
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
RTI Elec
|
|
°F
|
UL 746 |
|
RTI Imp
|
|
°F
|
UL 746 |
|
RTI Str
|
|
°F
|
UL 746 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
|
ohms
|
IEC 60093 |
|
Volume Resistivity
|
|
ohms·cm
|
ASTM D257, IEC 60093 |
|
Dielectric Strength
|
|||
|
0.0630 in, in Oil
|
|
V/mil
|
ASTM D149 |
|
0.126 in, in Air
|
|
V/mil
|
ASTM D149 |
|
0.0315 in, in Oil
|
|
V/mil
|
IEC 60243-1 |
|
0.0630 in, in Oil
|
|
V/mil
|
IEC 60243-1 |
|
0.126 in, in Oil
|
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant
|
|||
|
100 Hz
|
|
|
ASTM D150, IEC 60250 |
|
1 MHz
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
IEC 60250 |
|
60 Hz
|
|
|
IEC 60250 |
|
1 MHz
|
|
|
IEC 60250 |
|
Dissipation Factor
|
|||
|
100 Hz
|
|
|
ASTM D150, IEC 60250 |
|
1 MHz
|
|
|
ASTM D150 |
|
50 Hz
|
|
|
IEC 60250 |
|
60 Hz
|
|
|
IEC 60250 |
|
1 MHz
|
|
|
IEC 60250 |
|
Arc Resistance 11
|
|
|
ASTM D495 |
|
Comparative Tracking Index (CTI)
|
|
|
UL 746 |
|
Comparative Tracking Index
|
IEC 60112 | ||
|
--
|
|
V
|
|
|
Solution B
|
|
V
|
|
|
High Amp Arc Ignition (HAI) 12
|
|
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR)
|
|
|
UL 746 |
|
Hot-wire Ignition (HWI)
|
|
|
UL 746 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.016 in
|
|
|
|
|
0.028 in
|
|
|
|
|
0.08 in
|
|
|
|
|
Glow Wire Flammability Index (0.04 in)
|
|
°F
|
IEC 60695-2-12 |
|
Oxygen Index
|
|
%
|
ISO 4589-2 |
| Related Terminology | |||
|
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland, SABIC Innovative Plastics
|
|||
| Uses | |||
|
Uses may also be described by the following terms: Medical Applications, Food Applications, Electrical Applications, Electronic Applications, Electrical/Electronic Applications, Electrical Sector, Electronic Displays.
|
|||
| Automotive Specifications | |||
|
This plastic material has approval for 2 automotive specifications from the following agencies (the number in parentheses shows the number of specifications for that agency): CHRYSLER (1), GM (1).
|
|||
| Available Documents | |||
|
Technical Datasheet
|
|||
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
|
°F
|
|
|
Drying Time
|
|
hr
|
|
|
Suggested Max Moisture
|
|
%
|
|
|
Suggested Shot Size
|
|
%
|
|
|
Rear Temperature
|
|
°F
|
|
|
Middle Temperature
|
|
°F
|
|
|
Front Temperature
|
|
°F
|
|
|
Nozzle Temperature
|
|
°F
|
|
|
Processing (Melt) Temp
|
|
°F
|
|
|
Mold Temperature
|
|
°F
|
|
|
Back Pressure
|
|
psi
|
|
|
Screw Speed
|
|
rpm
|
|
|
Vent Depth
|
|
in
|
|
| Injection Notes | |||
|
Injection Molding Parameters
|
|||
| Notes |
| 1Typical properties: these are not to be construed as specifications. |
| 2Tensile Bar |
| 30.20 in/min |
| 4Type I, 0.20 in/min |
| 50.051 in/min |
| 60.079 in/min |
| 780*10*4 sp=62mm |
| 880*10*4 mm |
| 9120*10*4 mm |
| 10Rate A (50°C/h), Loading 2 (50 N) |
| 11Tungsten Electrode |
| 12Surface |
|
UL and the UL logo are trademarks of UL LLC © 2018. All Rights Reserved.
The information presented here was acquired by UL from the producer of the product or material or original information provider. However, UL assumes no responsibility or liability for the accuracy of the information contained on this website and strongly encourages that upon final product or material selection information is validated with the manufacturer. This website provides links to other websites owned by third parties. The content of such third party sites is not within our control, and we cannot and will not take responsibility for the information or content. |