Adiprene® L 100 Boletín técnico

Poliuretano (Poliéter, TDI)

Suministrado por Chemtura Corporation

Create your free Prospector account to view this complete product datasheet. A free account includes access to hundreds of thousands of detailed technical datasheets. Cree su cuenta gratuita
Descripción del Producto
ADIPRENE L 100 urethane elastomer is one of a series of liquid urethane polymers which can be cured to a strong, rubbery solid by reaction of the isocyanate groups with polyamine compounds. When cured with MBCA¹ curing agent, ADIPRENE L 100 yields vulcanizates in the 88 to 92 Shore A hardness range. Lower hardness values and special properties can be obtained with other curing systems. Cured ADIPRENE L 100 has high tensile strength and resilience, as well as excellent resistance to abrasion, compression set, oils, solvents, oxidation, ozone, and low temperatures.
General  
Estado del Material 
  • Comercial: Activo
Disponibilidad 
  • Asia-Pacífico
  • Europa
  • Latinoamérica
  • Norteamérica
 
Características 
  • Buena resistencia a la abrasión
  • Resilente
  • Resistencia alta a la tensión
  • Resistente a la oxidación
  • Resistente a las bajas temperaturas
  • Resistente al aceite
  • Resistente al disolvente
  • Resistente al ozono
Usos 
  • Aplicaciones de recubrimiento
Formas 
  • Líquido
Método de Procesamiento 
  • Fundición
  • Pulverización
 
Prop. físicas
Valor Típico
Unidad
Método de Ensayo
Densidad / Gravedad específica
 
ASTM D792
Contracción de moldeo - Flujo
in/in
ASTM D955
Elastómeros
Valor Típico
Unidad
Método de Ensayo
Resistencia a la tracción
    ASTM D412
Deformación del 100%
psi
 
Deformación del 300%
psi
 
Tensión
psi
ASTM D412
Elongación (Rotura)
%
ASTM D412
Resistencia al Rasgado
     
-- 2
lbf/in
ASTM D624
Ruptura
lbf/in
ASTM D470
Punto de Compresión (158°F, 22 hr)
%
ASTM D395B
Resiliencia Bayshore
%
ASTM D2632
Módulo Clash-Berg
    ASTM D1043
-70°F
psi
 
-40°F
psi
 
0°F
psi
 
75°F
psi
 
Dureza
Valor Típico
Unidad
Método de Ensayo
Dureza (Shore A)
 
ASTM D2240
Prop. térmicas
Valor Típico
Unidad
Método de Ensayo
Temperatura de fragilización
°F
ASTM D746
Coeficiente de dilatación térmica lineal (CLTE) - Flujo
    ASTM D696
-32 a 32°F
in/in/°F
 
32 a 75°F
in/in/°F
 
75 a 212°F
in/in/°F
 
212 a 302°F
in/in/°F
 
Conductividad térmica
Btu·in/hr/ft²/°F
ASTM C177
Termoendurecido
Valor Típico
Unidad
Método de Ensayo
Componentes termoendurecibles
     
Endurecedor
 
 
Resina
 
 
Vida útil (212°F)
min
 
Tiempo de desmoldeo (212°F)
min
 
Tiempo tras el curado (158°F)
hr
 
Información adicional
Valor Típico
Unidad
Método de Ensayo
Abrasion Index - NBS
 
 
Características
Características may also be described by the following terms: High Tensile Strength, Resilient, Good Abrasion Resistance, Abrasion Resistant, Oil Resistant, Solvent Resistant, Oxidation Resistant, Ozone Resistant, Low Temperature Resistant, Low Temperature Performance.
Usos
Usos may also be described by the following terms: Coating Applications.
Available Documents
Technical Datasheet (English)
Uncured Properties
Valor Típico
Unidad
Método de Ensayo
Curing Time (212°F)
hr
 
Notas
1Propiedades típicas: éstas no deben interpretarse como especificaciones.
2Cabezal C
 
UL y el logo de UL son marcas comerciales de UL LLC © 2020. Todos los derechos reservados.
La información presentada en este boletín técnico ha sido adquirida por UL Prospector del productor del material. UL Prospector realiza considerables esfuerzos para garantizar la exactitud de estos datos. No obstante, UL Prospector no asume responsabilidad alguna por los valores de los datos y recomienda encarecidamente que los datos del material se confirmen con el proveedor antes de la selección final.