Adiprene® LFP 1950A Boletín técnico

Polyurethane (Polyester, PPDI)

Suministrado por Chemtura Corporation

Create your free Prospector account to view this complete product datasheet. A free account includes access to hundreds of thousands of detailed technical datasheets. Cree su cuenta gratuita
Descripción del Producto
ADIPRENE LFP 1950A is a PPDI-terminated polyester prepolymer having very low free PPDI content (typical < 0.1%) for easier management of health and safety during handling. This prepolymer is similar to ADIPRENE PP 1095H in composition and performance, while offering significant processing advantages including easier melting, lower viscosity, and increased pour life. ADIPRENE LFP 1950A yields a high performance 93-95 Shore A hardness elastomer when cured with VIBRACURE® A 250.

The high performance features of ADIPRENE LFP 1950A are due to PPDI (p-phenylene diisocyanate), a special building block that imparts exceptional properties to cast polyurethane elastomers. The unique combination of properties exhibited by PPDI-based prepolymers is superior to those available from standard prepolymers based on TDI or MDI.

Features of ADIPRENE LFP 1950A include:
  • Low Free PPDI Content
  • Lower Viscosity and Easier Melting
  • Increased Pour Life
  • Excellent Dynamics
  • Excellent Tensile/Tear Strength
  • Excellent Resilience
General  
Estado del Material 
  • Comercial: Activo
Disponibilidad 
  • Asia-Pacífico
Características 
  • Buena resistencia al desgarro
  • Resilente
  • Resistencia alta a la tensión
  • Viscosidad baja
 
Método de Procesamiento 
  • Fundición
Prop. físicas
Valor Típico
Unidad
Método de Ensayo
Densidad / Gravedad específica
 
ASTM D792
Prop. mecánicas
Valor Típico
Unidad
Método de Ensayo
Resistencia a la compresión
    ASTM D695
5% Deformación
psi
 
10% Deformación
psi
 
15% Deformación
psi
 
20% Deformación
psi
 
25% Deformación
psi
 
Elastómeros
Valor Típico
Unidad
Método de Ensayo
Resistencia a la tracción
    ASTM D412
Deformación del 100%
psi
 
Deformación del 300%
psi
 
Tensión
psi
ASTM D412
Elongación (Rotura)
%
ASTM D412
Resistencia al Rasgado (Ruptura)
lbf/in
ASTM D470
Punto de Compresión
    ASTM D395B
158°F, 22 hr
%
 
212°F, 22 hr
%
 
Resiliencia Bayshore
%
ASTM D2632
Dureza
Valor Típico
Unidad
Método de Ensayo
Dureza (Shore A)
 
ASTM D2240
Termoendurecido
Valor Típico
Unidad
Método de Ensayo
Vida útil
min
 
Tiempo de desmoldeo
min
 
Tiempo tras el curado (241°F)
hr
 
Información adicional
Valor Típico
Unidad
Método de Ensayo
Dynamic Properties
     
Storage Modulus : 86°F
dynes/cm²
 
Storage Modulus : 302°F
dynes/cm²
 
Tangent Delta : 86°F
 
 
Tangent Delta : 302°F
 
 
Características
Características may also be described by the following terms: Low Viscosity, High Tensile Strength, Good Tear Strength, Resilient.
Available Documents
Technical Datasheet (English)
Notas
1Propiedades típicas: éstas no deben interpretarse como especificaciones.
 
UL y el logo de UL son marcas comerciales de UL LLC © 2020. Todos los derechos reservados.
La información presentada en este boletín técnico ha sido adquirida por UL Prospector del productor del material. UL Prospector realiza considerables esfuerzos para garantizar la exactitud de estos datos. No obstante, UL Prospector no asume responsabilidad alguna por los valores de los datos y recomienda encarecidamente que los datos del material se confirmen con el proveedor antes de la selección final.