Epoxi (epoxi) Propiedades típicas Generic Epoxy
|
This data represents typical values that have been calculated from all products classified as: Generic Epoxy
This information is provided for comparative purposes only.
|
|
Estado del Material
|
|
|
Disponibilidad
|
|
|
Densidad / Gravedad específica
|
|
|
|
|
--
|
0.637 a 2.00
|
|
ASTM D792 |
|
73°F
|
0.950 a 1.87
|
g/cm³
|
ISO 1183 |
|
--
|
1.07 a 1.22
|
g/cm³
|
ASTM D1505 |
|
Densidad aparente
|
0.60 a 1.60
|
g/cm³
|
ASTM D1895 |
|
Spiral Flow
|
18.4 a 74.8
|
in
|
|
|
Contracción de moldeo -
Flujo
(73°F)
|
1.0E-4 a 5.1E-3
|
in/in
|
ASTM D955 |
|
Absorción de agua (24 hr, 73°F)
|
0.010 a 0.31
|
%
|
ASTM D570 |
|
Viscosidad Mooney
|
45 a 96
|
MU
|
ASTM D1646 |
|
Contenido de Cloro
|
0.0 a 0.2
|
wt%
|
|
|
Módulo de tensión
|
|
|
|
|
73°F
|
115000 a 2.05E+6
|
psi
|
ASTM D638 |
|
73°F
|
5080 a 1.86E+6
|
psi
|
ISO 527-2 |
|
Tensión
|
|
|
ASTM D638 |
|
Punto de Fluencia, 73°F
|
1370 a 27600
|
psi
|
|
|
Rotura, 73°F
|
2860 a 35800
|
psi
|
|
|
73°F
|
0.900 a 12300
|
psi
|
|
|
Elongación
|
|
|
ASTM D638 |
|
Punto de Fluencia, 73°F
|
0.40 a 6.7
|
%
|
|
|
Rotura, 73°F
|
0.63 a 23
|
%
|
|
|
Módulo de Flexión
|
|
|
|
|
73°F
|
170 a 565000
|
psi
|
ASTM D790 |
|
73°F
|
400000 a 509000
|
psi
|
ISO 178 |
|
Resistencia a la flexión
|
|
|
|
|
73°F
|
0.996 a 20800
|
psi
|
ASTM D790 |
|
73°F
|
14500 a 20300
|
psi
|
ISO 178 |
|
Punto de Fluencia, 73°F
|
4010 a 38400
|
psi
|
ASTM D790 |
|
Módulo de compresión
|
3130 a 406000
|
psi
|
ASTM D695 |
|
Resistencia a la compresión
|
|
|
|
|
73°F
|
2430 a 16700
|
psi
|
ASTM D695 |
|
73°F
|
11400 a 17000
|
psi
|
ISO 604 |
|
Resistencia al corte (73°F)
|
565 a 7750
|
psi
|
ASTM D732 |
|
Resistencia al impacto Charpy sin entalle (73°F)
|
2.0 a 24
|
ft·lb/in²
|
ISO 179 |
|
Resistencia al Impacto Izod con ranura (73°F)
|
0.34 a 2.8
|
ft·lb/in
|
ASTM D256 |
|
Impacto Izod sin entalle (73°F)
|
0.44 a 0.82
|
ft·lb/in
|
ASTM D256 |
|
Dureza
|
|
|
|
|
73°F
|
73 a 92
|
|
ASTM D2240 |
|
73°F
|
80 a 91
|
|
ISO 868 |
|
Dureza Barcol
|
60 a 89
|
|
ASTM D2583 |
|
Temperatura de deflexión bajo carga
|
|
|
|
|
66 psi, No recocido
|
113 a 273
|
°F
|
ASTM D648 |
|
66 psi, No recocido
|
140 a 216
|
°F
|
ISO 75-2/B |
|
264 psi, No recocido
|
112 a 482
|
°F
|
ASTM D648 |
|
Temperatura de transición vítrea
|
|
|
|
|
--
|
91.2 a 312
|
°F
|
ASTM E1356 |
|
--
|
110 a 259
|
°F
|
ISO 11357-2 |
|
--
|
-59.8 a 392
|
°F
|
DSC |
|
Coeficiente de dilatación térmica lineal (CLTE) -
Flujo
|
|
|
|
|
--
|
3.2E-6 a 7.6E-5
|
in/in/°F
|
ASTM D696 |
|
--
|
1.4E-5 a 7.6E-5
|
in/in/°F
|
ASTM E831 |
|
--
|
1.1E-5 a 9.3E-5
|
in/in/°F
|
ISO 11359-2 |
|
Conductividad térmica (73°F)
|
0.43 a 12
|
Btu·in/hr/ft²/°F
|
ASTM C177 |
|
Resistividad superficial
|
4.0E+10 a 7.5E+15
|
ohms
|
ASTM D257 |
|
Resisitividad específica de volumen (73°F)
|
1.5E-4 a 5.0E+15
|
ohms·cm
|
ASTM D257 |
|
Resistencia dieléctrica (73°F)
|
150 a 1000
|
V/mil
|
ASTM D149 |
|
Constante dieléctrica
|
|
|
|
|
73°F
|
3.16 a 5.31
|
|
ASTM D150 |
|
73°F
|
2.90 a 7.80
|
|
IEC 60250 |
|
Factor de disipación
|
|
|
|
|
73°F
|
0.0 a 0.040
|
|
ASTM D150 |
|
73°F
|
8.4E-3 a 0.051
|
|
IEC 60250 |
|
Resistencia al arco
|
177 a 180
|
sec
|
ASTM D495 |
|
Índice de oxígeno
|
30 a 34
|
%
|
ASTM D2863 |
|
Índice de refracción
|
1.490 a 1.576
|
|
ASTM D542 |
|
Transmitancia
|
0.0 a 99.0
|
%
|
ASTM D1003 |
|
Vida útil (73°F)
|
1.0 a 3300
|
min
|
|
|
Vida útil en depósito
|
24 a 54
|
wk
|
|
|
Viscosidad de mezcla termoendurecida
|
10.0 a 23500
|
cP
|
ASTM D2393 |
|
Tiempo de desmoldeo
|
3.0 a 1600
|
min
|
|
|
Tiempo tras el curado
|
0.50 a 7.7
|
hr
|
|
|
Mix Ratio by Weight (PBW)
|
1.0 a 100
|
|
|
|
Mix Ratio by Volume (PBV)
|
1.0 a 100
|
|
|
|
Solids Content
|
99 a 100
|
%
|
|
|
Densidad (73°F)
|
0.868 a 1.55
|
g/cm³
|
|
|
Viscosidad (73°F)
|
0.015 a 20
|
Pa·s
|
|
|
Curing Time (73°F)
|
0.50 a 38
|
hr
|
|
|
Gel Time (73°F)
|
0.33 a 36
|
min
|
|
|
Vida útil (73°F)
|
3.9 a 3300
|
min
|
|
|
Vida útil en depósito
|
1 a 12
|
month
|
|
|
Absorción de agua (73°F)
|
0.047 a 0.12
|
%
|
|
|
Dureza Shore (73°F)
|
65 a 96
|
|
|
|
Lap Shear Strength (73°F)
|
1940 a 2020
|
psi
|
|
|
Tensión (73°F)
|
2600 a 10600
|
psi
|
|
|
Elongación en el Punto de Ruptura (73°F)
|
2.0 a 10
|
%
|
|
|
Resistencia a la compresión (73°F)
|
7800 a 17400
|
psi
|
|
|
Resistencia eléctrica (73°F)
|
370 a 570
|
V/mil
|
|
|
Permitividad relativa (73°F)
|
4.77
|
|
|
|
Resisitividad específica de volumen (73°F)
|
7.0E-5 a 1.2E+15
|
ohms·cm
|
|
|
Factor de disipación (73°F)
|
3.0E-3 a 0.031
|
|
|
|
Breakdown Voltage (73°F)
|
250 a 840
|
V/mil
|
|
| 1Propiedades típicas: éstas no deben interpretarse como especificaciones. |
| |
|
|