Epoxy Typical Properties Generic Epoxy

Product Description
This data represents typical values that have been calculated from all products classified as: Generic Epoxy

This information is provided for comparative purposes only.
General  
Material Status 
  • Commercial: Active
Availability 
  • Africa & Middle East
  • Asia Pacific
  • Europe
  • Latin America
  • North America
Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity
     
--
0,637 to 2,00
 
ASTM D792
73°F
0,950 to 1,87
g/cm³
ISO 1183
--
1,07 to 1,22
g/cm³
ASTM D1505
Apparent (Bulk) Density
0,60 to 1,60
g/cm³
ASTM D1895
Spiral Flow
18,4 to 74,8
in
 
Molding Shrinkage - Flow (73°F)
1,0E-4 to 5,1E-3
in/in
ASTM D955
Water Absorption (24 hr, 73°F)
0,010 to 0,31
%
ASTM D570
Mooney Viscosity
45 to 96
MU
ASTM D1646
Chlorine Content
0,0 to 0,2
wt%
 
Mechanical
Nominal Value
Unit
Test Method
Tensile Modulus
     
73°F
115000 to 2,05E+6
psi
ASTM D638
73°F
5080 to 1,86E+6
psi
ISO 527-2
Tensile Strength
    ASTM D638
Yield, 73°F
1370 to 27600
psi
 
Break, 73°F
2860 to 35800
psi
 
73°F
0,900 to 12300
psi
 
Tensile Elongation
    ASTM D638
Yield, 73°F
0,40 to 6,7
%
 
Break, 73°F
0,63 to 23
%
 
Flexural Modulus
     
73°F
170 to 565000
psi
ASTM D790
73°F
400000 to 509000
psi
ISO 178
Flexural Strength
     
73°F
0,996 to 20800
psi
ASTM D790
73°F
14500 to 20300
psi
ISO 178
Yield, 73°F
4010 to 38400
psi
ASTM D790
Compressive Modulus
3130 to 406000
psi
ASTM D695
Compressive Strength
     
73°F
2430 to 16700
psi
ASTM D695
73°F
11400 to 17000
psi
ISO 604
Shear Strength (73°F)
565 to 7750
psi
ASTM D732
Impact
Nominal Value
Unit
Test Method
Charpy Unnotched Impact Strength (73°F)
2,0 to 24
ft·lb/in²
ISO 179
Notched Izod Impact (73°F)
0,34 to 2,8
ft·lb/in
ASTM D256
Unnotched Izod Impact (73°F)
0,44 to 0,82
ft·lb/in
ASTM D256
Hardness
Nominal Value
Unit
Test Method
Durometer Hardness
     
73°F
73 to 92
 
ASTM D2240
73°F
80 to 91
 
ISO 868
Barcol Hardness
60 to 89
 
ASTM D2583
Thermal
Nominal Value
Unit
Test Method
Deflection Temperature Under Load
     
66 psi, Unannealed
113 to 273
°F
ASTM D648
66 psi, Unannealed
140 to 216
°F
ISO 75-2/B
264 psi, Unannealed
112 to 482
°F
ASTM D648
Glass Transition Temperature
     
--
91,2 to 312
°F
ASTM E1356
--
110 to 259
°F
ISO 11357-2
--
-59,8 to 392
°F
DSC
CLTE - Flow
     
--
3,2E-6 to 7,6E-5
in/in/°F
ASTM D696
--
1,4E-5 to 7,6E-5
in/in/°F
ASTM E831
--
1,1E-5 to 9,3E-5
in/in/°F
ISO 11359-2
Thermal Conductivity (73°F)
0,43 to 12
Btu·in/hr/ft²/°F
ASTM C177
Electrical
Nominal Value
Unit
Test Method
Surface Resistivity
4,0E+10 to 7,5E+15
ohms
ASTM D257
Volume Resistivity (73°F)
1,5E-4 to 5,0E+15
ohms·cm
ASTM D257
Dielectric Strength (73°F)
150 to 1000
V/mil
ASTM D149
Dielectric Constant
     
73°F
3,16 to 5,31
 
ASTM D150
73°F
2,90 to 7,80
 
IEC 60250
Dissipation Factor
     
73°F
0,0 to 0,040
 
ASTM D150
73°F
8,4E-3 to 0,051
 
IEC 60250
Arc Resistance
177 to 180
sec
ASTM D495
Flammability
Nominal Value
Unit
Test Method
Oxygen Index
30 to 34
%
ASTM D2863
Optical
Nominal Value
Unit
Test Method
Refractive Index
1,490 to 1,576
 
ASTM D542
Transmittance
0,0 to 99,0
%
ASTM D1003
Thermoset
Nominal Value
Unit
Test Method
Pot Life (73°F)
1,0 to 3300
min
 
Shelf Life
24 to 54
wk
 
Thermoset Mix Viscosity
10,0 to 23500
cP
ASTM D2393
Demold Time
3,0 to 1600
min
 
Post Cure Time
0,50 to 7,7
hr
 
Uncured Properties
Nominal Value
Unit
Test Method
Mix Ratio by Weight (PBW)
1,0 to 100
 
 
Mix Ratio by Volume (PBV)
1,0 to 100
 
 
Solids Content
99 to 100
%
 
Density (73°F)
0,868 to 1,55
g/cm³
 
Viscosity (73°F)
0,015 to 20
Pa·s
 
Curing Time (73°F)
0,50 to 38
hr
 
Gel Time (73°F)
0,33 to 36
min
 
Pot Life (73°F)
3,9 to 3300
min
 
Shelf Life
1 to 12
month
 
Cured Properties
Nominal Value
Unit
Test Method
Water Absorption (73°F)
0,047 to 0,12
%
 
Shore Hardness (73°F)
65 to 96
 
 
Lap Shear Strength (73°F)
1940 to 2020
psi
 
Tensile Strength (73°F)
2600 to 10600
psi
 
Tensile Elongation at Break (73°F)
2,0 to 10
%
 
Compressive Strength (73°F)
7800 to 17400
psi
 
Electric Strength (73°F)
370 to 570
V/mil
 
Relative Permittivity (73°F)
4,77
 
 
Volume Resistivity (73°F)
7,0E-5 to 1,2E+15
ohms·cm
 
Dissipation Factor (73°F)
3,0E-3 to 0,031
 
 
Breakdown Voltage (73°F)
250 to 840
V/mil
 
Notes
1Typical properties: these are not to be construed as specifications.