Epoxy Typical Properties Generic Epoxy - Unspecified

Product Description
This data represents typical values that have been calculated from all products classified as: Generic Epoxy - Unspecified

This information is provided for comparative purposes only.
General  
Material Status 
  • Commercial: Active
Availability 
  • Africa & Middle East
  • Asia Pacific
  • Europe
  • Latin America
  • North America
Filler / Reinforcement 
  • Filler
Physical
Nominal Value
Unit
Test Method
Density / Specific Gravity
1,27 to 2,21
 
ASTM D792
Spiral Flow
22,8 to 43,7
in
 
Molding Shrinkage - Flow (73°F)
3,0E-4 to 0,011
in/in
ASTM D955
Water Absorption (24 hr, 73°F)
0,080 to 1,3
%
ASTM D570
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (73°F)
870 to 11800
psi
ASTM D638
Tensile Elongation (Break, 73°F)
0,90 to 3,6
%
ASTM D638
Flexural Modulus (73°F)
1,84E+6 to 2,91E+6
psi
ASTM D790
Flexural Strength (73°F)
14300 to 21100
psi
ASTM D790
Compressive Strength (73°F)
5000 to 40000
psi
ASTM D695
Hardness
Nominal Value
Unit
Test Method
Durometer Hardness
     
73°F
64 to 90
 
ASTM D2240
73°F
88 to 90
 
ISO 868
Thermal
Nominal Value
Unit
Test Method
Glass Transition Temperature
248 to 356
°F
ISO 11357-2
CLTE - Flow
     
--
1,2E-5 to 5,0E-5
in/in/°F
ASTM D696
--
3,9E-6 to 4,2E-5
in/in/°F
ISO 11359-2
Thermal Conductivity (73°F)
4,1 to 6,1
Btu·in/hr/ft²/°F
ASTM C177
Electrical
Nominal Value
Unit
Test Method
Volume Resistivity (73°F)
3,5 to 1,2E+16
ohms·cm
ASTM D257
Dielectric Strength (73°F)
240 to 480
V/mil
ASTM D149
Dielectric Constant
     
73°F
2,80 to 4,93
 
ASTM D150
73°F
3,20 to 4,97
 
IEC 60250
Dissipation Factor
     
73°F
3,0E-3 to 0,035
 
ASTM D150
73°F
3,0E-3 to 0,016
 
IEC 60250
Thermoset
Nominal Value
Unit
Test Method
Thermoset Mix Viscosity
2000 to 5400
cP
ASTM D2393
Post Cure Time
3,8 to 5,0
hr
 
Uncured Properties
Nominal Value
Unit
Test Method
Density (73°F)
0,938 to 2,11
g/cm³
 
Viscosity (73°F)
0,010 to 65
Pa·s
 
Curing Time (73°F)
14 to 42
hr
 
Pot Life (73°F)
35 to 1100
min
 
Shelf Life
6 to 12
month
 
Notes
1Typical properties: these are not to be construed as specifications.