Maleic Anhydride Grafted Polymer (MAH-g) Typical Properties Generic MAH-g

Product Description
This data represents typical values that have been calculated from all products classified as: Generic MAH-g

This information is provided for comparative purposes only.
General  
Material Status 
  • Commercial: Active
Availability 
  • Africa & Middle East
  • Asia Pacific
  • Europe
  • Latin America
  • North America
Physical
Nominal Value
Unit
Test Method
Density
     
73°F
0,870 to 0,960
g/cm³
ISO 1183
--
0,920 to 0,940
g/cm³
ASTM D1505
Melt Mass-Flow Rate (MFR)
     
190°C/2.16 kg
1,0 to 12
g/10 min
ASTM D1238
190°C/2.16 kg
1,3 to 12
g/10 min
ISO 1133
Mechanical
Nominal Value
Unit
Test Method
Tensile Strength (Break, 73°F)
1160 to 4090
psi
ASTM D638
Tensile Elongation (Break, 73°F)
60 to 1700
%
ASTM D638
Flexural Modulus (73°F)
2000 to 134000
psi
ASTM D790
Hardness
Nominal Value
Unit
Test Method
Durometer Hardness (73°F)
21 to 98
 
ASTM D2240, ISO 868
Thermal
Nominal Value
Unit
Test Method
Vicat Softening Temperature
104 to 264
°F
ASTM D1525
Melting Temperature (DSC)
145 to 268
°F
ISO 3146
Notes
1Typical properties: these are not to be construed as specifications.