This data represents typical values that have been calculated from all products classified as: Generic MABS
This information is provided for comparative purposes only.
|
|
Material Status
|
|
|
Availability
|
|
|
Density / Specific Gravity
|
|
|
|
|
--
|
1,06 to 1,11
|
|
ASTM D792 |
|
73°F
|
1,08 to 1,10
|
g/cm³
|
ISO 1183 |
|
Melt Mass-Flow Rate (MFR)
|
|
|
|
|
220°C/10.0 kg
|
2,0 to 25
|
g/10 min
|
ASTM D1238 |
|
220°C/10.0 kg
|
10 to 30
|
g/10 min
|
ISO 1133 |
|
Melt Volume-Flow Rate (MVR) (220°C/10.0 kg)
|
2,0 to 20
|
cm³/10min
|
ISO 1133 |
|
Molding Shrinkage
|
|
|
|
|
Flow
: 73°F
|
4,0E-3 to 5,6E-3
|
in/in
|
ASTM D955 |
|
Across Flow
: 73°F
|
4,0E-3 to 6,0E-3
|
in/in
|
ASTM D955 |
|
73°F
|
0,40 to 0,60
|
%
|
ISO 294-4 |
|
Tensile Modulus
|
|
|
|
|
73°F
|
279000 to 384000
|
psi
|
ASTM D638 |
|
73°F
|
273000 to 381000
|
psi
|
ISO 527-2 |
|
Tensile Strength
|
|
|
|
|
Yield, 73°F
|
5660 to 8560
|
psi
|
ASTM D638 |
|
Yield, 73°F
|
6030 to 8040
|
psi
|
ISO 527-2 |
|
Break, 73°F
|
4330 to 5690
|
psi
|
ASTM D638 |
|
Break, 73°F
|
4640 to 6960
|
psi
|
ISO 527-2 |
|
73°F
|
5800 to 8270
|
psi
|
ISO 527-2 |
|
Tensile Strain
|
|
|
|
|
Yield, 73°F
|
3,0 to 4,0
|
%
|
ISO 527-2 |
|
Break, 73°F
|
10 to 40
|
%
|
ASTM D638 |
|
Break, 73°F
|
5,0 to 21
|
%
|
ISO 527-2 |
|
Flexural Modulus
|
|
|
|
|
73°F
|
258000 to 413000
|
psi
|
ASTM D790 |
|
73°F
|
265000 to 397000
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
73°F
|
7790 to 13900
|
psi
|
ASTM D790 |
|
73°F
|
10100 to 10300
|
psi
|
ISO 178 |
|
Charpy Notched Impact Strength (73°F)
|
2,2 to 7,2
|
ft·lb/in²
|
ISO 179 |
|
Charpy Unnotched Impact Strength (73°F)
|
37 to 58
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact
|
|
|
|
|
73°F
|
1,1 to 3,1
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
5,1 to 6,7
|
ft·lb/in²
|
ISO 180 |
|
Rockwell Hardness
|
|
|
|
|
73°F
|
102 to 118
|
|
ASTM D785 |
|
73°F
|
102 to 116
|
|
ISO 2039-2 |
|
Ball Indentation Hardness
|
10200 to 13100
|
psi
|
ISO 2039-1 |
|
Heat Deflection Temperature
|
|
|
|
|
66 psi, Unannealed
|
178 to 198
|
°F
|
ISO 75-2/B |
|
66 psi, Annealed
|
185 to 201
|
°F
|
ISO 75-2/B |
|
264 psi, Unannealed
|
170 to 198
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
158 to 173
|
°F
|
ISO 75-2/A |
|
264 psi, Annealed
|
175 to 194
|
°F
|
ISO 75-2/A |
|
Vicat Softening Temperature
|
|
|
|
|
--
|
189 to 226
|
°F
|
ASTM D1525 |
|
--
|
187 to 221
|
°F
|
ISO 306 |
|
Dissipation Factor (73°F)
|
0,013 to 0,016
|
|
IEC 60250 |
|
Light Transmittance
|
85,6 to 90,1
|
%
|
ASTM D1003 |
|
Haze
|
1,00 to 3,40
|
%
|
ASTM D1003 |
|
Drying Temperature
|
158 to 185
|
°F
|
|
|
Drying Time
|
2,0 to 4,0
|
hr
|
|
|
Rear Temperature
|
365 to 428
|
°F
|
|
|
Middle Temperature
|
392 to 420
|
°F
|
|
|
Front Temperature
|
410 to 456
|
°F
|
|
|
Nozzle Temperature
|
417 to 464
|
°F
|
|
|
Processing (Melt) Temp
|
417 to 473
|
°F
|
|
|
Mold Temperature
|
121 to 145
|
°F
|
|
|
Injection Pressure
|
17500 to 22500
|
psi
|
|
|
Back Pressure
|
107 to 6530
|
psi
|
|
|
Screw Speed
|
45 to 100
|
rpm
|
|
|
This data represents typical values that have been calculated from all products classified as: Generic MABS
This information is provided for comparative purposes only.
|
| 1Typical properties: these are not to be construed as specifications. |
| |
|
|