This data represents typical values that have been calculated from all products classified as: Generic Phenolic
This information is provided for comparative purposes only.
|
|
Material Status
|
|
|
Availability
|
|
|
Density / Specific Gravity
|
|
|
|
|
--
|
1,32 to 1,52
|
|
ASTM D792 |
|
73°F
|
1,35 to 1,83
|
g/cm³
|
ISO 1183 |
|
Apparent (Bulk) Density
|
0,54 to 1,09
|
g/cm³
|
ASTM D1895 |
|
Bulk Factor
|
2,0 to 8,0
|
|
ASTM D1895 |
|
Molding Shrinkage
|
|
|
|
|
Flow
: 73°F
|
2,5E-3 to 0,013
|
in/in
|
ASTM D955 |
|
Across Flow
: 73°F
|
9,9E-3 to 0,012
|
in/in
|
ASTM D955 |
|
73°F
|
0,36 to 9,5
|
%
|
ISO 294-4 |
|
Water Absorption
|
|
|
|
|
24 hr, 73°F
|
0,040 to 1,9
|
%
|
ASTM D570 |
|
24 hr, 73°F
|
0,040 to 0,41
|
%
|
ISO 62 |
|
Equilibrium, 73°F
|
0,20 to 0,50
|
%
|
ASTM D570 |
|
Tensile Modulus (73°F)
|
1,00E+6 to 1,52E+6
|
psi
|
ASTM D638 |
|
Tensile Strength
|
|
|
|
|
Yield, 73°F
|
6980 to 8400
|
psi
|
ASTM D638 |
|
73°F
|
6920 to 11800
|
psi
|
ASTM D638 |
|
73°F
|
7950 to 12800
|
psi
|
ISO 527-2 |
|
Flexural Modulus (73°F)
|
924000 to 2,42E+6
|
psi
|
ISO 178 |
|
Flexural Strength
|
|
|
|
|
73°F
|
10000 to 29400
|
psi
|
ASTM D790 |
|
73°F
|
11300 to 17200
|
psi
|
ISO 178 |
|
Compressive Strength
|
|
|
|
|
73°F
|
6560 to 45500
|
psi
|
ASTM D695 |
|
73°F
|
26900 to 33600
|
psi
|
ISO 604 |
|
Charpy Notched Impact Strength (73°F)
|
0,76 to 2,9
|
ft·lb/in²
|
ISO 179 |
|
Notched Izod Impact (73°F)
|
0,28 to 1,3
|
ft·lb/in
|
ASTM D256 |
|
Unnotched Izod Impact (73°F)
|
0,30 to 0,41
|
ft·lb/in
|
ASTM D4812 |
|
Rockwell Hardness
|
|
|
|
|
73°F
|
42 to 112
|
|
ASTM D785 |
|
73°F
|
105 to 112
|
|
ISO 2039-2 |
|
Deflection Temperature Under Load
|
|
|
|
|
264 psi, Unannealed
|
303 to 381
|
°F
|
ASTM D648 |
|
264 psi, Unannealed
|
311 to 375
|
°F
|
ISO 75-2/A |
|
Melting Temperature
|
146 to 276
|
°F
|
|
|
RTI Elec
|
236 to 320
|
°F
|
UL 746B |
|
RTI Str
|
253 to 302
|
°F
|
UL 746B |
|
Volume Resistivity
|
|
|
|
|
73°F
|
1,1E+10 to 2,5E+13
|
ohms·cm
|
ASTM D257 |
|
73°F
|
8,4E+11 to 1,0E+13
|
ohms·cm
|
IEC 60093 |
|
Dielectric Strength
|
|
|
|
|
73°F
|
190 to 390
|
V/mil
|
ASTM D149 |
|
73°F
|
250 to 300
|
V/mil
|
IEC 60243-1 |
|
Dielectric Constant (73°F)
|
4,39 to 7,15
|
|
ASTM D150 |
|
Dissipation Factor (73°F)
|
0,038 to 0,095
|
|
ASTM D150 |
|
Arc Resistance
|
31,1 to 182
|
sec
|
ASTM D495 |
|
Comparative Tracking Index (CTI)
|
139 to 500
|
V
|
UL 746A |
|
Comparative Tracking Index
|
180 to 225
|
V
|
IEC 60112 |
|
High Amp Arc Ignition (HAI)
|
195 to 200
|
|
UL 746A |
|
High Voltage Arc Tracking Rate (HVTR)
|
0,0748 to 0,945
|
in/min
|
UL 746A |
|
Hot-wire Ignition (HWI)
|
7,6 to 300
|
sec
|
UL 746A |
|
Insulation Resistance (73°F)
|
1,0E+8 to 1,0E+11
|
ohms
|
IEC 60167 |
|
Solids Content
|
59 to 80
|
%
|
|
|
Density (73°F)
|
0,971 to 1,22
|
g/cm³
|
|
|
Viscosity (73°F)
|
7,5E-3 to 0,81
|
Pa·s
|
|
| 1Typical properties: these are not to be construed as specifications. |
| |
|
|