Commercial: Active

Africa & Middle East, Asia Pacific, Europe, Latin America, North America

Density / Specific Gravity, Density, Density, Melt Mass-Flow Rate (MFR), Melt Mass-Flow Rate (MFR), Melt Volume-Flow Rate (MVR), Mold Shrink, Linear-Flow, Mold Shrink, Linear-Trans, Molding Shrinkage, Dimensional Change, Water Absorption @ 24 hrs, Water Absorption 24h/23C, Water Absorption @ Sat., Water Absorption @ Equil, Water Absorption 23C/50RH, Moisture Content, Tensile Modulus, Tensile Modulus, Tensile Strength, Tensile Strength at Yield, Tensile Stress at Yield, Tensile Strength at Break, Tensile Stress at Break, Tensile Stress, Tensile Elongation at Yield, Tensile Strain at Yield, Tensile Elongation at Break, Tensile Strain at Break, Flexural Modulus, Flexural Modulus, Flexural Strength, Flexural Stress, Flexural Strength at Yield, Coefficient of Friction, Film Thickness - Tested, Tensile Strength at Yield MD, Tensile Strength at Yield TD, Elongation at Break MD, Elongation at Break TD, Oxygen Transmission Rate, Water Vapor Transmission Rate, Tensile Stress at 100%, Tensile Stress at 300%, Tensile Strength at Break, Elongation at Break, Tear Strength, Charpy Notched Impact Strength, Charpy Unnotched Impact Strength, Notched Izod Impact, Notched Izod Impact (Area), Notched Izod Impact Strength, Unnotched Izod Impact, Unnotched Izod Impact Strength, Instrumented Dart Impact, Gardner Impact, Gardner Impact, Rockwell Hardness, Rockwell Hardness, Durometer Hardness, Shore Hardness, DTUL (66 psi) - Unannealed, DTUL (0.45 MPa) Unannealed, DTUL (66 psi) - Annealed, DTUL (264 psi) - Unannealed, DTUL (1.80 MPa) Unannealed, Continuous Use Temperature, Vicat Softening Temperature, Vicat Softening Temperature, Peak Melting Temperature, Melting Temperature (DSC), Melting Temperature, Melting Temperature, Melting Temperature, CLTE, Flow, Coefficient of Linear Thermal Expansion, Flow, Thermal Conductivity, Thermal Conductivity, RTI Elec, RTI Imp, RTI Str, Surface Resistivity, Surface Resistivity, Surface Resistivity, Volume Resistivity, Volume Resistivity, Dielectric Strength, Electric Strength, Dielectric Constant, Dielectric Constant, Relative Permittivity, Dissipation Factor, Dissipation Factor, Arc Resistance, Comparative Tracking Index (CTI), Comparative Tracking Index, High Amp Arc Ignition (HAI), High Voltage Arc Tracking Rate (HVTR), Hot-wire Ignition (HWI), Glow Wire Flammability Index, Glow Wire Ignition Temperature, Oxygen Index, Oxygen Index, Gloss, Opacity, Haze, Drying Temperature, Drying Time, Suggested Max Moisture, Suggested Max Regrind, Rear Temperature, Middle Temperature, Front Temperature, Nozzle Temperature, Processing (Melt) Temp, Mold Temperature, Injection Pressure, Holding Pressure, Back Pressure, Screw Speed, Cushion, Injection Notes, Drying Temperature, Drying Time, Suggested Max Regrind, Cylinder Zone 1 Temp., Cylinder Zone 2 Temp., Cylinder Zone 3 Temp., Cylinder Zone 4 Temp., Cylinder Zone 5 Temp., Adapter Temperature, Melt Temperature, Die Temperature, Extrusion Notes