ELVAX™ 660 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Composition - 12 % By Weight Vinyl Acetate comonomer content - Thermal Stabilizer: BHT antioxidant Applications - ELVAX™ resins can be used in a variety of applications involving molding, compounding, extrusion, adhesives, sealants, and wax blends.

ELVAX™ 670 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Composition - 12 % By Weight Vinyl Acetate comonomer content - Thermal Stabilizer: BHT antioxidant Applications - ELVAX™ resins can be used in a variety of applications involving molding, compounding, extrusion, adhesives, sealants, and wax blends.

ELVAX™ 750 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Composition - 9 % By Weight Vinyl Acetate comonomer content - Thermal Stabilizer: BHT antioxidant Applications - ELVAX™ resins can be used in a variety of applications involving molding, compounding, extrusion, adhesives, sealants, and wax blends.

ELVAX™ 760 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Composition - 9.3 % By Weight Vinyl Acetate - Thermal Stabilizer: BHT antioxidant Features - Low level BHT antioxidant Applications - ELVAX™ resins can be used in a variety of applications involving molding, compounding, extrusion, adhesives, sealants, and wax blends.

ELVAX™ 770 is an ethylene-vinyl acetate copolymer resin for use in industrial applications. Composition - 9.5 % By Weight Vinyl Acetate comonomer content - Thermal Stabilizer: BHT antioxidant Applications - ELVAX™ resins can be used in a variety of applications involving molding, compounding, extrusion, adhesives, sealants, and wax blends.

ELVAX™ CE9619-1 is an extrudable ethylene-vinyl acetate copolymer resin concentrate designed to modify the surface properties of films or coatings of ELVAX™ Resins or other compatible polymers. This is a concentrated masterbatch product and is designed to be blended with the resin to be modified. This concentrate contains 20 wt.% antiblock and 7 wt.% slip additives. It is available in in pellet form for use in conventional extrusion equipment designed to process polyethylene resins. Composition - 73% By Weight of an 18% By Weight Vinyl Acetate comonomer content resin - Thermal Stabilizer: BHT antioxidant - 7% By Weight Amide based slip agent - 20% By Weight Inorganic antiblock agent Features - This is a concentrated masterbatch product and is designed to be blended with other polymers. This resin is not intended to be extruded in its fure form. Applications - This resin is designed to modify the surface properties of films or coatings of ELVAX™ Resins or other compatible polymers.

AD 0433EH2 is a copolymer of ethylene and vinyl acetate.

Escorene Ultra AD 2528 is a very high flow rate, 27.6% VA copolymer, which is useful in formulating hot melt adhesives.

FL 00014 is a fractional MI copolymer of ethylene and vinyl acetate. For film requiring very high toughness, low creep, excellent optical properties and low gel.

FL 00018 is a fractional MI copolymer of ethylene and vinyl acetate. It offers combined toughness, good optical and sealing properties and low gel. In particular, its good behaviour in high frequency sealing, RF, is much appreciated.

FL 00112 is a fractional MI copolymer of ethylene and vinyl acetate offering low gel.

FL 00119 is a fractional MI copolymer of ethylene and vinyl acetate offering low gel.

FL 00206 is a copolymer of ethylene and vinyl acetate.

FL 00209 is a copolymer of ethylene and vinyl acetate. Processing Conditions Processing temperatures above 270 °C (518 °F) may cause resin degradation. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

FL 00212 is a copolymer of ethylene and vinyl acetate. Processing Conditions Processing temperatures above 260 °C (500 °F) may cause resin degradation. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

FL 00218 is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions Processing temperatures above 240 °C (464 °F) may cause resin degradation. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

FL 00226CC is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions Processing temperatures above 230 °C (446 °F) may cause resin degradation. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

FL 00328 is a copolymer of ethylene and vinyl acetate offering low gel. Processing Conditions Processing temperatures above 220 °C (428 °F) may cause resin degradation. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

FL 00623 is a good coextrusion partner in extrusion coating, blown and cast film. Excellent sealing material with a very low seal initiation temperature. Maximum processing temperature is 230°C (428°F).

FL 00714 is an easy processable grade for extrusion coating, co-extrusion coating and cast film. This grade offers excellent heat sealing characteristics and excellent optical properties. Processing Conditions Excellent results are obtained in extrusion coating at 240 °C (464°F) temperature range. Processing temperatures above 250°C (482°F) may cause resin degradation. FL00714 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

FL 00728CC is an excellent coextrusion partner in extrusion coating, blown and cast film. Good adhesion onto OPP in coextrusion. This grade offers excellent opticals, low gel and a very low Seal Initiation Temperature in sealing applications. Processing Conditions Excellent results are obtained in extrusion coating at 200 °C (392°F) temperature range. Processing temperatures above 220°C (428°F) may cause resin degradation. FL00728CC should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

FL 00909 is used in extrusion coating, cast film and co-extrusion . FL 00909 is a good sealing material with good optical properties. Processing Conditions Excellent results are obtained in extrusion coating at 250°C (482°F) temperature range. Processing temperatures above 270°C (518°F) may cause resin degradation. FL00909 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

FL 01418 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 01418 is an excellent sealing material with a very low seal initiation temperature and high clarity. Processing Conditions Excellent results are obtained in extrusion coating at 225 °C (437°F) temperature range. Processing temperatures above 240°C (464°F) may cause resin degradation. FL01418 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

FL 02020 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. FL 02020 is an excellent sealing material with a very low seal initiation temperature, high clarity, and low gel. Excellent results are obtained in extrusion coating at 220°C (428°F) temperature range. Processing temperatures above 240°C (464°F) may cause resin degradation. FL 02020 should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be purged with LDPE or a suitable cleaning compound before shutdown.

Escorene Ultra LD 705.MJ is a fractional melt index, 12.8 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and toughness.

Escorene Ultra LD 705.MJ is a fractional MI, 12.8% VA copolymer suitable for use in making blow molded articles, extruded profiles and compounds.

Escorene™ Ultra LD 708.NM is a 14.9 wt% vinyl acetate copolymer film resin. Films made from LD 708.NM resin exhibits good impact strength and superior heat sealability.

Escorene Ultra LD 713.93 is a 14.4 wt% vinyl acetate copolymer film resin. Film made from LD 713.93 exhibits very high impact strength, high clarity, and excellent heat sealability.

Escorene Ultra LD 713.93 is a 14.4 wt% vinyl acetate copolymer film resin. Film made from LD 713.93 exhibits very high impact strength, high clarity, and excellent heat sealability.

Escorene Ultra LD 713.93 is a 14.4% vinyl acetate copolymer with very good toughness, high clarity and excellent processability. It is suitable for use in making molded articles, extruded profiles and compounds.

Escorene™ Ultra LD 720 resins are high vinyl acetate copolymer specialty film resins designed for applications requiring outstanding heat sealability, along with excellent strength properties and toughness. These resins are also used in specialized molding applications.

Escorene Ultra LD 721.IK is a high vinyl acetate copolymer specialty film resin providing outstanding heat sealability, along with excellent strength properties and clarity.

Escorene Ultra LD 723.28 is a high vinyl acetate extrusion coating resin, which provides outstanding heat sealability and high clarity. LD 723.28 has a good balance of drawability and neck-in and can be coextruded with LDPE extrusion coating resins on most coextrusion coating lines.

Escorene Ultra LD 723.28 is an 18.5% vinyl acetate copolymer suitable for injection molding and compounding applications.

LD726.07 is primarily designed for high speed/low coating weight extrusion coating and is a good coextrusion partner with other polymers. LD726.07 is an excellent sealing material with a very low seal initiation temperature and high clarity.

Escorene Ultra LD727.22 is a high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.

Escorene™ Ultra LD 728 Series are high vinyl acetate copolymer resins with low melting temperature and excellent strength properties and toughness.

Escorene™ Ultra LD 730.NM is a 17.2 wt% vinyl acetate copolymer resin. LD 730.NM is designed to have superior strength and toughness combined with excellent optics and sealing properties.

Escorene™ Ultra LD 730.NM is a high vinyl acetate copolymer resin with low melting temperature and excellent strength properties and toughness.

Escorene Ultra LD 755 resins are a high vinyl acetate copolymers for specialty compounding applications and hot melt adhesives.