Produit | Disponibilité | Description du produit |
---|---|---|
DINALEN® 20 | Europe |
DINALEN® 20 is low density polyethylene containing no additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent.
DINALEN® 20 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.
DINALEN® 20 is extruded at recommended melt temperature range between 175°C and 200°C.
Recommended film thickness: 0.050 mm to 0.200 mm.
|
DINALEN® 30 | Europe |
DINALEN® 30 is low density polyethylene containing no additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent.
DINALEN® 30 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.
DINALEN® 30 is extruded at recommended melt temperature range between 165°C and 185°C.
Recommended film thickness: 0.030 mm to 0.100 mm.
|
DINALEN® 35 | Europe |
DINALEN® 35 is low density polyethylene containing additives. It is primarily intended for blow film extrusion while other processing techniques can be used to a lesser extent.
DINALEN® 35 exhibits excellent very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.
DINALEN® 35 is extruded at recommended melt temperature range between 165°C and 185°C.
Recommended film thickness: 0.030 mm to 0.100 mm.
|
DINALEN® 50 | Europe |
DINALEN 50 is low density polyethylene containing no additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent.
DINALEN 50 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.
DINALEN 50 is extruded at recommended melt temperature range between 160°C and 180° C. Recommended film thickness: 0.025 to 0.060 mm.
Application
- Thin non-slippery film of high gloss and transparency
- Heat shrinkable film with excellent stiffness for industrial bundling
- Extruded foams with physical blowing agent
- Small diameter pipe extrusion
- Wire and cable sheathing
- Injection moulded thick-walled products
- Blown packaging and other shallow objects
- Mixing and co-extrusion with suitable polyolefin grades
|
DINALEN® 55 | Europe |
DINALEN® 55 is low density polyethylene containing slip and anti-blocking additives. It is primarily intended for blow and cast film extrusion while other processing techniques can be used to a lesser extent.
DINALEN® 55 exhibits very good draw-down with good balance of stiffness, mechanical and optical properties of extruded film.
DINALEN® 55 is extruded at recommended melt temperature range between 160°C and 180°C. Recommended film thickness: 0.25 to 0.05mm.
Application
- Thin slippery film of high gloss and transparency
- Production of film for lamination
- Production of film for a variety of primary flexible packaging like FFS for foodstuffs, sanitary articles, chemicals
- Film production for a many kinds of carrier-bags, like airport security bags, DTK bags, cooler-bags, T-shirt-bags, shoulder-bags
- Blending with DINALEN 50 to obtain a less slippery film
- Mixing and co-extrusion with suitable i-polybutene-1 grades to produce film for peel systems
- Mixing and co-extrusion with suitable polyolefin grades
|
DINALEN® 65 | Europe |
DINALEN® 65 is low density polyethylene containing slip and anti-blocking additives. It is intended for thin blow film extrusion. Other processing techniques can be used in less extent.
DINALEN® 65 exhibits excellent processability, uniform optical and other properties, depending on its application. It is extruded at temperatures ranging from 140°C to 165°C.
DINALEN® 65 gives films of desired properties depending on selected processing parameters such as processing temperature and capacity; blowing ratio, and the height of the frost line. Recommended film thickness : 0.020 mm to 0.040 mm.
|
OKITEN® 222 A | Europe |
OKITEN® 222 A is low density polyethylene, without slip agent, intended for extrusion of haevy duty blown film.
OKITEN® 222 A is characterized by excellent processing properties and thermal stability. Extruded film has very good balance of stiffness, mechanical and optical properties.
|
OKITEN® 233 A | Europe |
OKITEN® 233 A is low density polyethylene, without slip agent, intended for extrusion of general purpose blown film.
OKITEN® 233 A is characterized by excellent processing properties and thermal stability. Extruded film has good mechanical properties.
|
OKITEN® 245 A | Europe |
OKITEN® 245 A is low density polyethylene, without slip agent, intended for extrusion of general purpose blown film of high transparency and gloss.
OKITEN® 245 A is characterized by excellent processing properties and thermal stability. Extruded film has good mechanical properties.
OKITEN® 245 A is extruded in temperature range from145°C to 170°C.
Recommended film thickness: 0.025 mm to 0.060 mm.
|
OKITEN® 245 S | Europe |
OKITEN® 245 S is low density polyethylene intended for extrusion of thin blown film having high slip properties.
OKITEN® 245 S is characterized by excellent processability and thermal stability; the extruded film exhibits high transparency and very good mechanical properties.
OKITEN® 245 S. is extruded in temperature range of 145°C to 170°C.
Recommended film thickness: 0.025 mm to 0.060mm.
|