Description: E1006 is a hot emulsion styrene-butadiene copolymer, polymerized using a fatty acid emulsifier and coagulated with salt-acid. It is a very light color product stabilized with a non-staining antioxidant. Applications: E1006 is recommended for light colored applications; for adhesives, tire white sidewalls, transport and transmission belts, sponge materials, sporting goods, flooring, colored shoe soles and heels.

Description: E1006CR is a crumb hot emulsion styrene-butadiene copolymer, polymerized using a fatty acid emulsifier and coagulated with salt-acid. It is a very light color product stabilized with a non-staining antioxidant, and presented as free flowing dusted crumb which eliminates the end for size reduction equipment. Between 7% and 12% of Calcium Carbonate is used as dusting agent. Applications: E1006CR is recommended for light colored applications; for adhesives, tire white sidewalls, transport and transmission belts, sponge materials, sporting goods, flooring, colored shoe soles and heels.

Description: E1009L is a hot emulsion styrene-butadiene copolymer, slightly cross-linked with divinylbenzene. It is polymerized using fatty acid as emulsifier, coagulated with salt acid and stabilized with a non-staining antioxidant. Applications: E1009L is a lower gel version of the e1009h it also reduces mill shrinkage and swelling in molding improving dimensional stability and outstanding surface texture of finished products. It is also widely used in sealants and adhesives giving good balance between adhesive and cohesive properties.

Description: E10101A is a cross-linked emulsion styrene-butadiene copolymer with divinyl benzene, using a mix of rosin and fatty acid as emulsifier. It is coagulated with Aluminum-acid and stabilized with a non-staining antioxidant. It is produced in acordance with good manufacturing practices and complies with FDA 21 CFR §175.300, §177.1210 and §178.3910 for use in food contact applications. Applications: E10101A gives excellent dimensional stability to compounds, reduces die swell and shrinkage in extruded products. It is also recommended for improving cohesive strength in adhesives and sealants which will be in contact with food or beverages.

Description: E10102 is a cold emulsion styrene-butadiene copolymer, polymerized with fatty acid and rosin acid emulsifier, coagulated by salt-acid system and stabilized with a non-staining antioxidant. Applications: El E10102 is widely used as raw material in tire and in various industrial products.

Description: E1011 is a hot emulsion styrene-butadiene copolymer using rosin acid as emulsifier and coagulated with salt- acid. It is very light color product stabilized with a non-staining antioxidant. Applications: E1011 gives excellent green tack and adhesive properties with good balance of mechanical strength. Is recommended for molded and extruded mechanical goods, adhesives, caulks and sealants.

Description: E1011CR is a crumb hot emulsion styrene-butadiene copolymer using rosin acid as emulsifier and coagulated with salt-acid. It is very light color product stabilized with a non-staining antioxidant. This rubber is produced as free flowing dusted crumb which eliminates the need for size reduction equipment. Between 4% and 12% of Calcium Carbonate is used as dusting agent. Applications: E1011CR gives excellent green tack and adhesive properties with good balance of mechanical strength. Is recommended for molded and extruded mechanical goods, adhesives, caulks and sealants.

Description: E1012 is a high viscosity hot emulsion styrene-butadiene copolymer, polymerized using a fatty acid emulsifier and coagulated with salt-acid. It is a very light color product stabilized with a non-staining antioxidant. Applications: E1012 is the high molecular weight version of e1006, particularly useful as a binder for fibrous materials and adhesives where increased cohesive strength is desired.

Description: E1012CR is a crumb high viscosity hot emulsion styrene butadiene copolymer, polymerized using fatty acid emulsifier and coagulated with salt-acid. It is very light color product stabilized with a non-staining antioxidant, and presented as free flowing dusted crumb which eliminates the end for size reduction equipment. Between 4% and 12% of Calcium Carbonate is used as dusting agent.

Description: E1013A is a styrene-butadiene copolymer, hot polymerized using a fatty acid soap. Previously to the alum-acid coagulation, a non-staining stabilizer is added in the manufacturing process. Applications: E1013A is suitable for adhesive applications it is particularly used for can-sealing compounds, tire liners, mechanical goods, including auto mounts, and household products.

Description: 10140 is a product manufactured by mixing a cold styrene-butadiene copolymer containing 5.5% bound styrene (80%) with high styrene resin latex (20%), coagulated by salt-acid system and stabilized with a non staining antioxidant. Applications: E10140 masterbach provides the user with an advantage through ease of processing and improved product quality, and it provides the stiffening effect to the final product. Is used in tires, footwear, sponges and other mechanical goods, etc.

Description: E1028A is a high styrene, hot emulsion styrene-butadiene copolymer using fatty acid as emulsifier and coagulated with salt-acid. It is stabilized with a non-staining antioxidant. The product does not contain nitrosamine promoters, and complies with FDA 21 CFR §175.300, §177.1210 and §178.3910 for use in food contact applications. Applications: E1028A is exceptionally light colored. It features high green strength, low air permeability and excellent flow properties, it is recommended for use in adhesives, sealants, tire liners, mechanical goods and household products.

Description: E1500A is a styrene-butadiene copolymer, cold polymerized using a rosin acid soap. Previously to the alum-acid coagulation, a non-staining stabilizer is added in the manufacturing process. The product does not contain nitrosamine promoters. Applications: E1500A is suitable for molded and extruded mechanical goods and sealants applications.

E1502 is a cold styrene-butadiene copolymer, used fatty and rosin acid as emulsifier, coagulated by salt-acid system and stabilized with a non-staining antioxidant. Applications: E1502 is widely used as raw material in tire, shoe sole and in various industrial products.

Description: E1502A is a styrene-butadiene copolymer, cold polymerized using fatty and rosin acid soap. Previously to the alum-acid coagulation, a non-staining stabilizer is added in the manufacturing process. The product does not contain nitrosamine promoters. Applications: E1502A is substitute of the natural rubber in wide range of compounds, offering advantages of light colour, uniformity and low levels of impurities. It´s good flow characteristics produce improvements in mixing and moulding behavior, it is used for food and pharmaceutical packaging and seals, baby bottle teats and health care, adhesives, chemical derivatives of rubbers. E1502A is manufactured to the highest standards but special requirements apply to certain sensitive applications such as food contact and pharmaceuticals. Reference should always be made to local legislation regulating these applications.

Description: E1502cr is a crumb styrene-butadiene copolymer, cold polymerized using fatty acid as emulsifier, coagulated by salt-acid system and stabilized with a non-staining antioxidant. This rubber is produced as free flowing dusted crumb wich eliminates the need for size reductions equipment. Between 4% and 12% of Calcium carbonate is used as dusting agent. Applications: E1502CR is widely used as raw material in tire, heels, shoe sole, in various industrial products and in the production of transaparent and light colored articles. As crumb it is used in the manufacturing of adhesives.

Description: E1509 is a cold styrene-butadiene copolymer, used fatty and rosin acid as emulsifier, coagulated by salt-acid system and stabilized with a non staining antioxidant. Applications: E1509 is used in shoe sole formulations, sponge, industrial products.

Description: E1509A is a copolymer styrene-butadiene, cold emulsion polymerized used fatty acid as emulsifier, coagulated by salt-acid system and stabilized with a non staining antioxidant. Applications: E1509A is recommended for mechanical goods and sealing applications.

E1712 is a copolymer styrene-butadiene cold emulsion polymerized used fatty acid as emulsifier, coagulated by salt-acid system and it is extended utilizing aromatic oil. Applications: E1712 is used in tire formulations and in a variety of industrial products due to its excellent adhesion and processing properties.

Description: E1732 is a copolymer styrene-butadiene, cold emulsion polymerized used fatty acid and rosin acid as emulsifier, coagulated by salt - acid system and it is extended utilizing naphthenic oil, thereby complying with the European directive 2005/69/EC. Applications: E1732 is used in the manufacture of tires and industrial products for its excellent processing properties.

Description: E1778 is a copolymer styrene-butadiene, cold emulsion polymerized used fatty acid as emulsifier, coagulated by salt-acid system and it is extended utilizing 37.5 parts of naphthenic oil. Applications: E1778 is used in the manufacture of tires and industrial products for its excellent processing properties.

Description: E1778R is a cold emulsion styrene-butadiene copolymer, polymerized using fatty acid as emulsifier, coagulated by salt-acid system and it is extended utilizing naphthenic oil and meets the European directive 2005/69/EC. Applications: E1778R is used in the manufacture of tires and industrial products for its excellent processing properties.

Description: E261 is a self-reinforcing emulsion rubber due to its high styrene content. The design of the elastomer allows for excellent processability during mixing and the special antioxidant used in its manufacture make it non-staining. Applications: E261 is used as a reinforcing agent that does not alter the final products specific gravity while increasing the hardness, rigidity, abrasive and tear resistance as well as improving the flexibility of vulcanized shoe-soles. This product can also be used as raw material in the manufacture of tires.