ADVANCENE™ EM-4925-AAH
ADVANCENE™ EM-4925-AAH HDPE Resin is specifically designed for use in either intermittent or continuous blow molding equipment to produce containers up to 30 liters in size - applications that require the combination of outstanding environmental stress crack resistance (ESCR) and high impact strength.
ADVANCENE™ EM-4925-AAH HDPE Resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g. detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.) health and medical aids. In addition, it can be blow molded into other thin-walled parts and houseware items, and can also be extruded into profiles or sheets.
Main Characteristics
ADVANCENE™ EM-4925-AAH HDPE Resin is also considered a multipurpose blow molding resin designed for the high speed production of blow molded containers used for packaging household industrial chemicals (e.g. detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.) health and medical aids. In addition, it can be blow molded into other thin-walled parts and houseware items, and can also be extruded into profiles or sheets.
Main Characteristics
- Outstanding environmental stress crack resistance.
- High impact strength.
- Good extrusion characteristics.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 ADVANCENE™ EM-4925-AAH 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
Commercial: Active
文档
description
Technical Datasheet (English)
下载文档可用性
Africa & Middle East, Europe, North America
用途
Containers
加工方式
Blow Molding
其他属性
Features, Density / Specific Gravity, Melt Mass-Flow Rate (MFR), Melt Mass-Flow Rate (MFR), Environmental Stress-Cracking Resistance (ESCR), Tensile Strength at Yield, Tensile Stress at Yield, Tensile Strength at Break, Tensile Stress at Break, Tensile Elongation at Yield, Tensile Strain at Yield, Tensile Elongation at Break, Tensile Strain at Break, Flexural Modulus, Flexural Modulus, Tensile Impact Strength, Tensile Impact Strength, Durometer Hardness, DTUL (66 psi) - Unannealed, DTUL (0.45 MPa) Unannealed, Brittleness Temperature, Brittleness Temperature, Vicat Softening Temperature, Vicat Softening Temperature, Peak Melting Temperature, Melting Temperature (DSC), Peak Crystallization Temperature (DSC), Peak Crystallization Temperature (DSC)
加工
Find specific processing information for ADVANCENE™ Polyethylene as well as general information for the Polyethylene, High Density generic family. 注册 或 登录 了解更多信息。