Karina COMP.PEBDL PRETO-FC (TC-L)
THE COMP. LDPE-L BLACK-FC-HSF (TCL) IS A BLACK LINEAR LOW DENSITY POLYETHYLENE COMPOUND, ESPECIALLY DEVELOPED FOR THE MANUFACTURE OF WIRELESS COATING AND CABLES.
PRESENTS EXCELLENT CHARACTERISTICS OF PROCESSING, MECHANICAL RESISTANCE AND RESISTANCE TO BREAK UNDER TENSION. TCL IS ADDITIVE WITH SMOKE BLACK, WHICH GUARANTEES RESISTANCE TO PHOTODEGRADATION WITH HIGH UV ABSORPTION COEFFICIENT.
LDPE-L IS NOT A HYPROSCOPIC MATERIAL, HOWEVER, BLACK-SMOKE, USED IN ITS ANTI-UV ADDITIVATION, ABSORBES MOISTURE FROM THE ENVIRONMENT. THEREFORE, ALL PEBD-L CONTAINING SMOKE BLACK IN THEIR FORMULATION MUST GO THROUGH A DRYING PROCESS BEFORE USING IT. DRYING MUST BE MADE FOR MINIMUM 2 H AT A TEMPERATURE OF 90 ° C. IN THESE CONDITIONS THE HUMIDITY LEVEL ACHIEVES A VALUE THAT, NORMALLY, DOES NOT HARM THE PROCESSING OF THE MATERIAL. USE OF THIS RESIN WITHOUT PRIOR DRYING MAY CAUSE PROBLEMS IN THE FINAL PRODUCT, LIKE BUBBLES AND / OR SURFACE SURFACE.
WE RECOMMEND THAT THE MATERIAL WILL BE CONSUMED BEFORE 365 DAYS AFTER THEIR MANUFACTURE.
PROCESSING CONDITIONS RECOMMENDED FOR EXTRUSION: - TEMPERATURE PROFILE: 160 TO 230°C.
THE BEST PROCESSING CONDITIONS MAY VARY ACCORDING TO THE TYPE OF EQUIPMENT USED AND SHOULD NOT BE CONSIDERED AS A PERFORMANCE GUARANTEE.
PRESENTS EXCELLENT CHARACTERISTICS OF PROCESSING, MECHANICAL RESISTANCE AND RESISTANCE TO BREAK UNDER TENSION. TCL IS ADDITIVE WITH SMOKE BLACK, WHICH GUARANTEES RESISTANCE TO PHOTODEGRADATION WITH HIGH UV ABSORPTION COEFFICIENT.
LDPE-L IS NOT A HYPROSCOPIC MATERIAL, HOWEVER, BLACK-SMOKE, USED IN ITS ANTI-UV ADDITIVATION, ABSORBES MOISTURE FROM THE ENVIRONMENT. THEREFORE, ALL PEBD-L CONTAINING SMOKE BLACK IN THEIR FORMULATION MUST GO THROUGH A DRYING PROCESS BEFORE USING IT. DRYING MUST BE MADE FOR MINIMUM 2 H AT A TEMPERATURE OF 90 ° C. IN THESE CONDITIONS THE HUMIDITY LEVEL ACHIEVES A VALUE THAT, NORMALLY, DOES NOT HARM THE PROCESSING OF THE MATERIAL. USE OF THIS RESIN WITHOUT PRIOR DRYING MAY CAUSE PROBLEMS IN THE FINAL PRODUCT, LIKE BUBBLES AND / OR SURFACE SURFACE.
WE RECOMMEND THAT THE MATERIAL WILL BE CONSUMED BEFORE 365 DAYS AFTER THEIR MANUFACTURE.
PROCESSING CONDITIONS RECOMMENDED FOR EXTRUSION: - TEMPERATURE PROFILE: 160 TO 230°C.
THE BEST PROCESSING CONDITIONS MAY VARY ACCORDING TO THE TYPE OF EQUIPMENT USED AND SHOULD NOT BE CONSIDERED AS A PERFORMANCE GUARANTEE.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Karina COMP.PEBDL PRETO-FC (TC-L) 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
description
Technical Datasheet (English)
下载文档可用性
拉丁美洲
用途
电话绝缘体
其他属性
特性, 密度 / 比重, 熔流率（熔体流动速率）, 炭黑含量, 拉伸断裂强度, 断裂伸长率, 脆化温度, 机械性能变化, 其他性能
加工
Find specific processing information for Karina as well as general information for the 线性低密度聚乙烯 generic family. 注册 或 登录 了解更多信息。
购买地点
您可以從 1 個經銷商或製造商處購買 Karina COMP.PEBDL PRETO-FC (TC-L)。 注册 或 登录 了解更多信息。