Karina COMP. PEBD PRETO-FC (TC9008)
COMPOUND PEBD PRETO (TC 9008) IS A LOW DENSITY POLYETHYLENE COMPOUND, WITH HIGH MOLECULAR WEIGHT AND MOLECULAR WEIGHT
DISTRIBUTION, SPECIALLY DEVELOPED TO WIRE & CABLE JACKETING.
THIS GRADE SHOW GOOD EXTRUDABILITY, MECHANICAL RESISTANCE AND STRESS CRACKING. IT CONTAINS CARBON BLACK TO RESIST
PHOTODEGRADATION AND HIGH UV ABSORPTION COEFFICIENT.
ACCORDING TO ASTM D 1248:04, TC9008 IS IC-5 CLASSIFIED, E9 DEGREE, J4 E W4.
CAS REGISTRY NUMBER: 9002-88-4.
LDPE IS NOT A HYGROSCOPIC MATERIAL. HOWEVER, CARBON BLACK, WHICH IS USED AS AN ANTI-UV ADDITIVE, ABSORBS MOISTURE FROM THE
ENVIRONMENT. THEREFORE, ALL HDPE CONTAINING CARBON BLACK IN ITS COMPOSITION MUST BE DRIED BEFORE USE. THE DRYING PROCESS
MUST BE MADE AT LEAST FOR 2 HOURS AT 90°C. UNDER THESE CONDITIONS THE AMOUNT OF MOISTURE DECREASES TO VALUES THAT WILL NOT
INTERFERE IN THE PROCESSABILITY OF THE RESIN. THE USE OF THIS RESIN WITHOUT PREVIOUS DRYING MAY CAUSE PROBLEMS IN THE FINISHED
PRODUCT, SUCH AS BLISTERING AND/OR ROUGHNESS OF THE SURFACE.
DISTRIBUTION, SPECIALLY DEVELOPED TO WIRE & CABLE JACKETING.
THIS GRADE SHOW GOOD EXTRUDABILITY, MECHANICAL RESISTANCE AND STRESS CRACKING. IT CONTAINS CARBON BLACK TO RESIST
PHOTODEGRADATION AND HIGH UV ABSORPTION COEFFICIENT.
ACCORDING TO ASTM D 1248:04, TC9008 IS IC-5 CLASSIFIED, E9 DEGREE, J4 E W4.
CAS REGISTRY NUMBER: 9002-88-4.
LDPE IS NOT A HYGROSCOPIC MATERIAL. HOWEVER, CARBON BLACK, WHICH IS USED AS AN ANTI-UV ADDITIVE, ABSORBS MOISTURE FROM THE
ENVIRONMENT. THEREFORE, ALL HDPE CONTAINING CARBON BLACK IN ITS COMPOSITION MUST BE DRIED BEFORE USE. THE DRYING PROCESS
MUST BE MADE AT LEAST FOR 2 HOURS AT 90°C. UNDER THESE CONDITIONS THE AMOUNT OF MOISTURE DECREASES TO VALUES THAT WILL NOT
INTERFERE IN THE PROCESSABILITY OF THE RESIN. THE USE OF THIS RESIN WITHOUT PREVIOUS DRYING MAY CAUSE PROBLEMS IN THE FINISHED
PRODUCT, SUCH AS BLISTERING AND/OR ROUGHNESS OF THE SURFACE.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Karina COMP. PEBD PRETO-FC (TC9008) 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
description
Technical Datasheet (English)
下载文档可用性
拉丁美洲
用途
电话绝缘体
加工方式
挤出
其他属性
特性, 密度 / 比重, 熔流率（熔体流动速率）, 炭黑含量, 拉伸断裂强度, 断裂伸长率, 脆化温度, 机械性能变化, 其他性能
加工
Find specific processing information for Karina as well as general information for the 聚乙烯，低密度 generic family. 注册 或 登录 了解更多信息。
购买地点
您可以從 1 個經銷商或製造商處購買 Karina COMP. PEBD PRETO-FC (TC9008)。 注册 或 登录 了解更多信息。