VESTORAN® 1900 S27024
As a material of amorphous structure VESTORAN® 1900 S27024 shows very small mold shrinkage. Therefore molded parts have a very low tendency to warp. The impact modified compound is of low density and easy to process.
Further properties are excellent impact strength, heat deflection under load and suitability for being coated with lacquers.
Moldings of VESTORAN® 1900 S27024 are dimensionally stable and hydrolysis resistant even in hot water, but are more sensitive to organic solvents than semi-crystalline plastics.
VESTORAN® 1900 S27024 is resistant to aqueous alkalines and acides, certain alcohols, and glycol solutions and particularly suitable for the adhesion promoter-free manufacturing of plastic/ rubber composites by the Evonik Industries AG -patented K&K process.
Pigmentation may affect values.
Further properties are excellent impact strength, heat deflection under load and suitability for being coated with lacquers.
Moldings of VESTORAN® 1900 S27024 are dimensionally stable and hydrolysis resistant even in hot water, but are more sensitive to organic solvents than semi-crystalline plastics.
VESTORAN® 1900 S27024 is resistant to aqueous alkalines and acides, certain alcohols, and glycol solutions and particularly suitable for the adhesion promoter-free manufacturing of plastic/ rubber composites by the Evonik Industries AG -patented K&K process.
Pigmentation may affect values.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 VESTORAN® 1900 S27024 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
可用性
北美洲, 欧洲
用途
Composites
加工方式
注射成型
其他属性
添加剂, 特性, 外观, 形式, 密度 / 比重, 密度, 熔融体积流量（MVR）, 收缩率, 拉伸模量, 拉伸屈服应力, 拉伸断裂应力, 拉伸应力, 拉伸屈服应变, 标称拉伸断裂应变, 弯曲模量, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, DTUL (0.45 MPa) 未退火, DTUL (1.80 MPa) 未退火, 维卡软化温度, 体积电阻率, 介电强度, 相对电容率, 耗散因数, 漏电起痕指数, 可燃性等级, 加工（熔体）温度, 模具温度