Additive manufacturing Polycarbonate blend (PC + ABS) for fused filament fabrication. Diameter: 1.75 mm Optimized for printability. Smooth surface finish. Tough and rigid, impact and heat resistant, cold stable until -30 °C, UV stable. Particularly suitable for outdoor applications e.g. jigs & fixtures in harsh environments.

Additive manufacturing Polycarbonate blend (PC + ABS) for fused filament fabrication. Diameter: 2.85 mm Optimized for printability. Smooth surface finish. Tough and rigid, impact and heat resistant, cold stable until -30 °C, UV stable. Particularly suitable for outdoor applications e.g. jigs & fixtures in harsh environments.

Additive manufacturing Polycarbonate blend (PC + ABS) for fused filament fabrication. Diameter: 1.75 mm Optimized for printability. Smooth surface finish. Tough and rigid, impact and heat resistant, cold stable until -30 °C, UV stable. Particularly suitable for outdoor applications e.g. jigs & fixtures in harsh environments.

Additive manufacturing Polycarbonate blend (PC + ABS) for fused filament fabrication. Diameter: 2.85 mm Optimized for printability. Smooth surface finish. Tough and rigid, impact and heat resistant, cold stable until -30 °C, UV stable. Particularly suitable for outdoor applications e.g. jigs & fixtures in harsh environments.

Additive manufacturing Polycarbonate grade for filament extrusion. Recycled grade made from pre-consumer material. High viscous, high strength, transparent.

Additive manufacturing Polycarbonate grade for filament extrusion. Transparent, tough and rigid; easy processing, low viscosity

MVR (330°C/2.16kg) 25 cm³/10 min; high viscosity; UV stabilized; softening temperature (VST/B 120)=159°C; injection molding - melt temperature 320 - 340°C

MVR (330°C/2.16kg) 45 cm³/10 min; easy release; softening temperature (VST/B 120)=158°C; injection molding - melt temperature 320 - 340°C; Covers for brake lights and indicator lights; Headlamp reflectors/bezels

MVR (330°C/2.16kg) 17 cm³/10 min; easy release; suitable for superheated steam sterilisation up to 143°C as well as for pharmaceutical applications according to United States Pharmacopeia (USP) XXII Class VI; softening temperature (VST/B 120)=170°C; injection molding - melt temperature 320 - 340°C; Films for medical packaging; Contact lens holders; Medical vessels; Safety valve for respiration aids; Syringe tops

MVR (330°C/2.16kg) 30 cm³/10 min; easy release; low viscosity; 'softening temperature (VST/B 120)=173°C; injection molding - melt temperature 320 - 340°C; Covers for brake lights and indicator lights; Headlamp reflectors/bezels

MVR (330°C/2.16kg) 10 cm³/10 min; high viscosity; UV stabilized; 'softening temperature (VST/B 120)=184°C; injection molding - melt temperature 330 - 340°C; Covers for brake lights and indicator lights; car interior light covers; Domestic lamp covers; Headlamp lenses; Covers for ships' lights; Connector pieces for halogen systems

MVR (330°C/2.16kg) 18 cm³/10 min; easy release; 'softening temperature (VST/B 120)=183°C; injection molding - melt temperature 330 - 340°C; Covers for brake lights and indicator lights; Recessed light fixtures/reflectors; Raised brake lights; Headlamp reflectors/bezels

MVR (330°C/2.16kg) 18 cm³/10 min; easy release; UV stabilized; 'softening temperature (VST/B 120)=182°C; injection molding - melt temperature 330 - 340°C; Lamp covers; Headlamp lenses

MVR (330°C/2.16kg) 8 cm³/10 min; high viscosity; easy release; 'softening temperature (VST/B 120)=203°C; injection molding - melt temperature 330 - 340°C; Covers for brake lights and indicator lights; Recessed light fixtures/reflectors; Blade-type fuses; Headlamp reflectors/bezels

MVR (330°C/2.16kg) 8 cm³/10 min; high viscosity; easy release; UV stabilized; 'softening temperature (VST/B 120)=202°C; injection molding - melt temperature 330 - 340°C; Lamp covers; Headlamp lenses

(PC+ABS)-Blend; Vicat/B 120 temperature = 113°C; for electroplating applications

Rubber modified PC blend; 10 % mineral filled; flame retardant; Vicat/B 120 temperature = 108°C; extrusion grade; good extrusion and vacuum-forming behaviour; UL-recognition 94 V-0 at 0.75mm; glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; high heat resistance; Vicat/B 120 temperature = 136°C; ball indentation temperature >= 125°C; UL recognition 94 V-0 at 1.5 mm; suitable as supporting material for energized parts

(PC+ABS)-Blend; easy flowing; Vicat/B 120 temperature = 103°C; UL recognition 94 V-0 at 1.5 mm; no juicing; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 97°C; compared to FR3000 improved chemical resistance and stress cracking behavior; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 97°C; UL recognition 94 V-0 at 1.5 mm; Glow wire test: 960°C at 2.0 mm; no juicing; good light stability

(PC+ABS)-Blend; Vicat/B 120 temperature = 103°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 99°C; UL recognition 94 V-0 (1.0 mm); glow wire temperature (GWFI): 960°C at 2.0 mm; for notebooks and thinwall applications

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 89°C; improved chemical resistance; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; very easy-flowing; Vicat/B 120 temperature = 96°C; UL recognition 94 V-0 at 1.5 mm; Components for the electrical/electronics sector

(PC+ABS)-Blend; flame retardant; very easy-flowing; Vicat/B 120 temperature = 96°C; UL recognition 94 V-0 at 1.5 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 108°C; easy flow version of FR3006; increased heat resistance; UL recognition 94 V-1 at 1.5 mm, V-0 at 1.8 mm and 5VB at 1.8 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; improved chemical and very good hydrolysis resistance; HDT/A >= 85°C; UL recognition 94 V-0 at 1.5 mm; Glow wire test: 960°C at 2.0 mm; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; improved chemical and very good hydrolysis resistance; HDT/A >= 85°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; good light stability Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; improved chemical and very good hydrolysis resistance; HDT/A >= 85°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 103°C; UL recognition 94 5VB at 1.8 mm; successor to FR3000 BBS066; Improved hydrolysis resistance

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 108°C; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; optimized processability; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 108°C; increased heat resistance; UL recognition 94 5VB (1.5 mm); glow wire temperature (GWFI): 960°C at 2.0 mm

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 110°C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; improved chemical resistance and stress cracking behavior; successor to FR2010 Partially bio-circular grade / Attributed via mass balance (according to ISCC PLUS Standard).

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 110°C; increased heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; improved chemical resistance and stress cracking behavior; successor to FR2010

(PC+ABS)-Blend; flame retardant; easy flowing; Vicat/B 120 temperature = 118°C; good heat resistance; UL recognition 94 V-0 at 1.5 mm; glow wire temperature (GWFI): 960°C at 2.0 mm; good light stability

(PC+ABS)-Blend; flame retardant; Vicat/B 120 temperature = 102°C; UL recognition 94 V-1 (1.5 mm); good light stability

(PC+ABS)-Blend; flame retardant; impact modified; easy flowing; Vicat/B 120 temperature = 95°C; for: information technology

(PC-I)-Blend; flame retardant; Vicat/B 120 temperature = 101 °C; UL-recognition 94 V-0 at 0.75mm; rated f1 per UL746 C "Outdoor Suitability"; improved colorability compared to other PC+ASA grades

mineral filled PC blend; 5 % mineral filled; UV-stabilized; Vicat/B 120 temperature = 102°C; flame-retardant;; UL recognition 94 V-0 (0.6mm); low smoke density