LEXAN™ Copolymer EXL1330 - Americas

Família genérica: Polycarbonate • Fornecido por: SABIC

LEXAN EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1330 resin is a general purpose product available in a wide range of opaque colors and is an excellent candidate for a broad range of applications.

Propriedades gerais

Acesse os detalhes completos da ficha de dados de LEXAN™ Copolymer EXL1330 - Americas quando você criar sua conta gratuita no Prospector. Você encontrará informações completas sobre especificações físicas, mecânicas e de dureza

Status do material

Commercial: Active

Documentos

E121562 - SABIC INNOVATIVE PLASTICS US L L C

Baixar o documento

E121562 - SABIC INNOVATIVE PLASTICS US L L C

Baixar o documento

LNP™ EXL COPOLYMER RESINS FOR HEALTHCARE

Baixar o documento

Visualize mais 2 documentos

Download More Documents

Disponibilidade

Latin America, North America

Usos

Aerospace Applications

Método de processamento

Injection Molding

Dados multipontosa

Compressive Stress vs. Strain (ASTM D6641)
Flexural DMA (ASTM D5023)
Specific Heat vs. Temperature (ASTM E1269)
Specific Volume vs. Temperature (PVT)
Tensile Stress vs. Strain (ASTM D638)
Thermal Conductivity vs. Temperature (ASTM E1530)
Viscosity vs. Shear Rate (ASTM D3835)

Outras propriedades

Features, Also Available In, Density / Specific Gravity, Density, Melt Mass-Flow Rate (MFR), Melt Volume-Flow Rate (MVR), Molding Shrinkage, Water Absorption Sat/23C, Water Absorption 23C/50RH, Outdoor Suitability, Tensile Modulus, Tensile Modulus, Tensile Strength at Yield, Tensile Stress at Yield, Tensile Strength at Break, Tensile Stress at Break, Tensile Elongation at Yield, Tensile Strain at Yield, Tensile Elongation at Break, Tensile Strain at Break, Flexural Modulus, Flexural Modulus, Flexural Stress, Flexural Strength at Yield, Charpy Notched Impact Strength, Charpy Unnotched Impact Strength, Notched Izod Impact, Notched Izod Impact Strength, Unnotched Izod Impact Strength, Instrumented Dart Impact, Ball Indentation Hardness, DTUL (66 psi) - Unannealed, DTUL (0.45 MPa) Unannealed, DTUL (264 psi) - Unannealed, DTUL (1.80 MPa) Unannealed, Vicat Softening Temperature, Vicat Softening Temperature, Ball Pressure Test, CLTE, Flow (TMA), Coefficient of Linear Thermal Expansion, Flow, CLTE, Transverse (TMA), Coefficient of Linear Thermal Expansion, Transverse, RTI Elec, RTI Imp, RTI Str, Comparative Tracking Index (CTI), High Amp Arc Ignition (HAI), Hot-wire Ignition (HWI), Flame Rating, Glow Wire Flammability Index, Glow Wire Ignition Temperature, Oxygen Index, Drying Temperature, Drying Time, Suggested Max Moisture, Suggested Shot Size, Rear Temperature, Middle Temperature, Front Temperature, Nozzle Temperature, Processing (Melt) Temp, Mold Temperature, Back Pressure, Screw Speed, Vent Depth, Injection Notes, Extrusion Notes

Acesse as propriedades 67 em Plásticos. Crie sua conta gratuita ou faça login no Prospector.

Processamento

Encontre informações de processamento específicas para LEXAN™ Copolymer, além de informações gerais para a família genérica Polycarbonate. Inscreva-se ou Faça login para mais informações.

Onde comprar

Você pode adquirir LEXAN™ Copolymer EXL1330 - Americas de 5 distribuidores ou fabricantes. Inscreva-se ou Faça login para mais informações.

Características Premium

Encontre Yellow Cards da UL

Os Yellow Cards da UL são uma garantia de segurança e qualidade reconhecida globalmente, uma demonstração certificada de que os plásticos cumprem um conjunto específico de credenciais de desempenho.

Encontre Yellow Cards da UL