ULTEM™ Resin 9090 - Americas 数据表

聚醚酰亚胺

用SABIC提供

Create your free Prospector account to view this complete product datasheet. A free account includes access to hundreds of thousands of detailed technical datasheets. 创建您的免费帐号
产品说明
Polyetherimide Blend with improved Ductility and Detergent resistance. Meets FAR 25.853 and OSU 55/55 heat release and provides low toxicity, smoke and flame evolution.
总览  
材料状态 
  • 已商用:当前有效
供货地区 
  • 北美洲
  • 拉丁美洲
 
用途 
  • Additive Manufacturing (3D Printing)
  • Rail Applications
  • 飞机内饰
Also Available In 
  • Europe
物理性能
额定值
单位制
测试方法
密度 / 比重
     
--
 
ASTM D792
--
g/cm³
ISO 1183
熔流率(熔体流动速率) (337°C/6.6 kg)
g/10 min
ASTM D1238
熔融体积流量(MVR) (360°C/5.0 kg)
cm³/10min
ISO 1133
收缩率 - 流动 (0,126 in)
%
内部方法
机械性能
额定值
单位制
测试方法
拉伸模量 2
psi
ASTM D638
抗张强度
     
屈服 3
psi
ASTM D638
屈服
psi
ISO 527-2/50
断裂 3
psi
ASTM D638
断裂
psi
ISO 527-2/50
伸长率
     
屈服 3
%
ASTM D638
屈服
%
ISO 527-2/50
断裂 3
%
ASTM D638
断裂
%
ISO 527-2/50
弯曲模量
     
1,97 in 跨距 4
psi
ASTM D790
-- 5
psi
ISO 178
弯曲应力
     
-- 5, 6
psi
ISO 178
屈服, 1,97 in 跨距 4
psi
ASTM D790
冲击性能
额定值
单位制
测试方法
简支梁缺口冲击强度 (73°F)
ft·lb/in²
ISO 179/2C
悬壁梁缺口冲击强度
     
73°F
ft·lb/in
ASTM D256
-22°F 7
ft·lb/in²
ISO 180/1A
73°F 7
ft·lb/in²
ISO 180/1A
无缺口伊佐德冲击强度 7
    ISO 180/1U
-22°F
 
 
73°F
 
 
反向缺口冲击 (0,126 in)
ft·lb/in
ASTM D256
装有测量仪表的落镖冲击
    ASTM D3763
-4°F, Total Energy
in·lb
 
32°F, Total Energy
in·lb
 
73°F, Total Energy
in·lb
 
Instrumented Impact, Ductility
    ASTM D3763
-4°F
%
 
32°F
%
 
73°F
%
 
热性能
额定值
单位制
测试方法
载荷下热变形温度
     
66 psi, 未退火, 0,252 in
°F
ASTM D648
66 psi, 未退火, 0,157 in, 3,94 in 跨距 8
°F
ISO 75-2/Be
264 psi, 未退火, 0,252 in
°F
ASTM D648
264 psi, 未退火, 0,157 in, 3,94 in 跨距 8
°F
ISO 75-2/Ae
维卡软化温度
     
--
°F
ISO 306/B120, ISO 306/B50
--
°F
ISO 306/A50
线形热膨胀系数
     
流动 : -4 到 302°F
in/in/°F
ASTM E831
流动 : 73 到 302°F
in/in/°F
ISO 11359-2
垂直 : -4 到 302°F
in/in/°F
ASTM E831
垂直 : 73 到 302°F
in/in/°F
ISO 11359-2
导热系数
Btu·in/hr/ft²/°F
ASTM C177
可燃性
额定值
单位制
测试方法
极限氧指数
%
ASTM D2863
NBS Smoke Density - Flaming, Ds  9
 
ASTM E662
OSU峰值放热速率 - 5 minute test
kW/m²
FAR 25.853
OSU总放热量 - 2 minute test
kW·min/m²
FAR 25.853
Vertical Burn - a, 60s, passes at
sec
FAR 25.853
Related Terminology
This supplier and product may also be known by these terms: GE Plastics, LNP Engineering Plastics, GE Polymerland, SABIC Innovative Plastics, SABIC Americas, Saudi Basic Industries Corporation
用途
用途 may also be described by the following terms: Aircraft Interiors, Additive Manufacturing, 3D Printing,3-D Printing, Rail Applications, Railway, Train.
注射
额定值
单位制
 
干燥温度
°F
 
干燥时间
hr
 
建议的最大水分含量
%
 
建议注射量
%
 
料筒后部温度
°F
 
料筒中部温度
°F
 
料筒前部温度
°F
 
射嘴温度
°F
 
加工(熔体)温度
°F
 
模具温度
°F
 
背压
psi
 
螺杆转速
rpm
 
排气孔深度
in
 
注射说明
Injection Molding Parameters
  • Drying Time (Cumulative): 24 hrs
备注
1一般属性:这些不能被视为规格。
20,20 in/min
3类型 1, 0,20 in/min
40,051 in/min
50,079 in/min
6at Yield
780*10*4 mm
8120*10*4 mm
94 min
 
UL 和 UL 徽标为 UL LLC © 的商标 2020。保留所有权利。
此数据表中的信息由 UL Prospector 从该材料的生产商处获得。UL Prospector 尽最大努力确保此数据的准确性。 但是 UL Prospector 对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。