VESTAMID® L2124 NC is a plasticized, heat- and light- stabilized polyamide 12 compound for the extrusion of flexible tubing and hoses especially for oil and petrochemical applications.
Tubing according to DIN 73 378, Type: PA 12-PHL.
VESTAMID® L2124 NC is characterized by a high melt viscosity and good dimensional control during pipe extrusion.
Properties of compounds based on PA12 vary little with changing humidity due to low moisture absorption. Parts made of this semi-crystalline material are characterized by exceptional impact strength, low coefficient of friction and good chemical resistance.
Pigmentation may affect values.
Tubing according to DIN 73 378, Type: PA 12-PHL.
VESTAMID® L2124 NC is characterized by a high melt viscosity and good dimensional control during pipe extrusion.
Properties of compounds based on PA12 vary little with changing humidity due to low moisture absorption. Parts made of this semi-crystalline material are characterized by exceptional impact strength, low coefficient of friction and good chemical resistance.
Pigmentation may affect values.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 VESTAMID® L L2124 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
Comercial: Activo
可用性
Europa, Norteamérica
用途
Aplicaciones de automoción
汽车规格
FORD WSK-M4D701-A
加工方式
Extrusión
其他属性
添加剤, 特徴, 外観, 形状, 密度 / 比重, 密度, メルトボリュームフローレート（MVR）, 成形収縮, 給水率 平衡/23℃, 吸水率 23℃/50ＲＨ, 引張弾性率, 引張降伏応力, 引張破壊応力, 引張り応力, 引張り降伏歪み, 引張り破壊呼び歪み, 引張クリープ係数 1時間, 引張クリープ係数 1000時間, 曲げ弾性率, 曲げ強度, シャルピー衝撃強度（ノッチ付）, シャルピー衝撃強度（ノッチなし）, DTUL (0.45 MPa) アニールなし, DTUL (1.80 MPa) アニールなし, ビカット軟化温度, ピーク溶融温度, 溶解温度, 線膨張係数、平行, 線膨張係数、垂直, 表面抵抗性, 体積抵抗率, 耐電圧, 比誘電率, 拡散率, 耐トラッキング性, 燃焼性の区分, その他の特性, 成形（溶融）温度, 金型温度, 射出圧力
加工
Find specific processing information for VESTAMID® L Polyamide 12 as well as general information for the Polyamide 12 generic family. 注册 或 登录 了解更多信息。