VESTAMID® NRG 2901 BK
For Gas pipes Fittings
VESTAMID® NRG 2901 BK is a high viscosity, heat stabilized compound with exceptional mold release properties. Additionally VESTAMID® NRG 2901 BK is nucleated to reduce the cycle time and shrinkage of molded parts.
Generally mechanical properties of compounds based on PA 12 vary little with changing humidity due to their low moisture absorption. Parts made of this semi-crystalline material are characterized by exceptional impact strength, high abrasion resistance, low friction and good chemical resistance.
VESTAMID® NRG 2901 BK is a high viscosity, heat stabilized compound with exceptional mold release properties. Additionally VESTAMID® NRG 2901 BK is nucleated to reduce the cycle time and shrinkage of molded parts.
Generally mechanical properties of compounds based on PA 12 vary little with changing humidity due to their low moisture absorption. Parts made of this semi-crystalline material are characterized by exceptional impact strength, high abrasion resistance, low friction and good chemical resistance.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 VESTAMID® NRG 2901 BK 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
已商用：当前有效
文档
description
Technical Datasheet (English)
下载文档可用性
北美洲, 欧洲
用途
管道
加工方式
管路挤出成型
其他属性
添加剂, 特性, 外观, 形式, 密度 / 比重, 密度, 熔融体积流量（MVR）, 收缩率, 吸水率23C/50RH, 拉伸模量, 拉伸屈服应力, 拉伸应力, 拉伸屈服应变, 拉伸断裂应变, 标称拉伸断裂应变, 弯曲模量, 弯曲应力, 简支梁缺口冲击强度, 简支梁无缺口冲击强度, DTUL (0.45 MPa) 未退火, DTUL (1.80 MPa) 未退火, 玻璃转化温度, 维卡软化温度, 熔融温度, 干燥温度, 干燥时间, 加工（熔体）温度, 模具温度
加工
Find specific processing information for VESTAMID® NRG Polyamide 12 as well as general information for the 聚酰胺 12 generic family. 注册 或 登录 了解更多信息。