Stanyl® TW200F6
30% Glass Reinforced, Heat Stabilized
Stanyl® TW200F6 is a high heat polyamide that offers excellent creep resistance, strength, stiffness and fatigue resistance, not only at ambient temperatures but especially at high temperatures, while at the same time providing cycle-time advantages and excellent flow.
Stanyl® TW200F6 is a high heat polyamide that offers excellent creep resistance, strength, stiffness and fatigue resistance, not only at ambient temperatures but especially at high temperatures, while at the same time providing cycle-time advantages and excellent flow.
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Stanyl® TW200F6 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
供給可能
文档
layers
檢視超過 10 個文件
Download More Documents可用性
アジア太平洋地域, アフリカ＆中東, ラテンアメリカ, 北アメリカ, 欧州
汽车规格
CHRYSLER MS-DB-41
加工方式
射出成形
多点数据
- Isochronous Stress vs. Strain (ISO 11403)
- Isothermal Stress vs. Strain (ISO 11403)
- LTHA-Strain at Break vs. Time (ISO 11403)
- LTHA-Stress at Break vs. Time (ISO 11403)
- Secant Modulus vs. Strain (ISO 11403)
- Shear Modulus vs. Temperature, Dynamic (ISO 11403)
- Shear Stress vs. Shear Rate (ISO 11403)
- Specific Volume vs Temperature (ISO 11403)
- Tensile Fatigue
- Tensile Modulus vs. Temperature (ISO 11403)
- Tensile Modulus vs. Temperature, Dynamic (ISO 11403)
- Viscosity vs. Shear Rate (ISO 11403)
其他属性
フィラー／強化剤, 添加剤, 特徴, 樹脂ID, 密度, スパイラルフロー, 成形収縮, 吸水率 24h/23℃, 給水率 平衡/23℃, 吸水率 23℃/50ＲＨ, 粘度数, 引張弾性率, 引張破壊応力, 引張り破壊歪み, 曲げ弾性率, 曲げ強度, シャルピー衝撃強度（ノッチ付）, シャルピー衝撃強度（ノッチなし）, ノッチ付アイゾット衝撃強度, DTUL (0.45 MPa) アニールなし, DTUL (1.80 MPa) アニールなし, ガラス転移温度, ビカット軟化温度, ボール圧力試験, 溶解温度, 線膨張係数、平行, 線膨張係数、垂直, RTI 電気, RTI 衝撃, RTI 強度, 表面抵抗性, 体積抵抗率, 耐電圧, 比誘電率, 拡散率, 耐トラッキング性, 燃焼定格, 燃焼性の区分, グローワイヤ燃焼指数, グローワイヤ着火温度, 酸素指数, 溶融密度, 溶融比熱, 溶融熱伝導性, その他の特性
加工
Find specific processing information for Stanyl® Polyamide 46 as well as general information for the Polyamide 46 generic family. 注册 或 登录 了解更多信息。