Vectra® A435

通用系列： Liquid Crystal Polymer • 提供方： Celanese Corporation

Glass/PTFE, best High Arc Ignition performance
Best High Current Arc Ignition (HAI) performance. Glass/PTFE filled. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant. UL-Listing V-0 in natural at 044mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C. UL = Underwriters Laboratories (USA)

一般属性

使用 Prospector 建立免費帳戶時，可造訪 Vectra® A435 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊

物料形态

Comercial: Activo

文档

E83005 - CELANESE INTERNATIONAL CORP

下载文档

可用性

África y Oriente Medio, Asia-Pacífico, Europa, Latinoamérica, Norteamérica

加工方式

Injection Molding

多点数据

Isothermal Stress vs. Strain (ISO 11403)
Secant Modulus vs. Strain (ISO 11403)
Shear Modulus vs. Temperature, Dynamic (ISO 11403)

其他属性

Additive, Features, Forms, Density, Molding Shrinkage, Water Absorption 23C/50RH, Tensile Modulus, Tensile Stress at Break, Tensile Strain at Break, Flexural Modulus, Flexural Stress, Compressive Modulus, Compressive Stress, Charpy Notched Impact Strength, Charpy Unnotched Impact Strength, Notched Izod Impact Strength, Unnotched Izod Impact Strength, Rockwell Hardness, DTUL (0.45 MPa) Unannealed, DTUL (1.80 MPa) Unannealed, DTUL (8.00 MPa) Unannealed, Melting Temperature, Coefficient of Linear Thermal Expansion, Flow, Coefficient of Linear Thermal Expansion, Transverse, Surface Resistivity, Volume Resistivity, Electric Strength, Relative Permittivity, Dissipation Factor, Arc Resistance, Comparative Tracking Index (CTI), Flame Rating, Additional Properties, Drying Temperature, Drying Time, Suggested Max Moisture, Hopper Temperature, Rear Temperature, Middle Temperature, Front Temperature, Nozzle Temperature, Processing (Melt) Temp, Mold Temperature, Injection Rate, Back Pressure

访问塑料中的 \45 个属性。创建您的免费帐户或登录 Prospector。