Vectra® C130
30% glass fiber, higher temp. capability & easier flow than A130
Has the same excellent balance of properties as A130 with higher temperature capability and easier flow. Slightly more dimensional stability in vapor phase soldering than A130. Suitable for some infrared SMT applications. 30% glass reinforced. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural and black at 0.38mm thickness per UL 94 flame testing, and UL-5VA in natural at 1.5mm. Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 220°C at 0.75mm. UL = Underwriters Laboratories (USA)
Has the same excellent balance of properties as A130 with higher temperature capability and easier flow. Slightly more dimensional stability in vapor phase soldering than A130. Suitable for some infrared SMT applications. 30% glass reinforced. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural and black at 0.38mm thickness per UL 94 flame testing, and UL-5VA in natural at 1.5mm. Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 220°C at 0.75mm. UL = Underwriters Laboratories (USA)
一般属性
使用 Prospector 建立免費帳戶時，可造訪 Vectra® C130 的完整資料表詳細資訊。您將找到有關物理、機械和硬度規格的完整資訊
物料形态
Commercial : actif
文档
可用性
Afrique & Moyen-Orient, Amérique du Nord, Amérique latine, Asie Pacifique, Europe
加工方式
Moulage par injection
多点数据
- Isothermal Stress vs. Strain (ISO 11403)
- Secant Modulus vs. Strain (ISO 11403)
- Shear Modulus vs. Temperature, Dynamic (ISO 11403)
其他属性
Charge / Renforcement, Additif, Caractéristiques, Formes, Densité, Retrait au moulage, Module de traction, Contrainte de traction à la rupture, Allongement en traction à la rupture, Module de fluage en traction 1h, Module de fluage en traction 1000h, Module de flexion, Résistance à la flexion, Module d'élasticité en compression, Contrainte de compression, Essai de résilience Charpy avec entaille, Résilience en flexion Izod avec entaille, Dureté Rockwell, DTUL (0.45 MPa) non recuit, DTUL (1.80 MPa) non recuit, DTUL (8.00 MPa) non recuit, Température de fusion, Coefficient d'expansion thermique linéaire, écoulement, Coefficient d'expansion thermique linéaire, transversal, Résistivité de surface, Résistivité de volume, Rigidité diélectrique, Permittivité relative, Facteur de dissipation, Résistance à l'arc, Indice de cheminement comparatif (CTI) , Degré d'inflammabilité - UL, Indice limite d'oxygène, Propriétés supplémentaires, Température de séchage, Temps de séchage, Humidité maxi recommandée, Température de trémie, Température arrière, Température centrale, Température avant, Température de buse, Température de traitement (fusion), Température de moulage, Vitesse d'injection, Contre pression
加工
Find specific processing information for Vectra® LCP as well as general information for the Polymère de cristal liquide generic family. 注册 或 登录 了解更多信息。